Celstran PA6 PA6-GF60-03
添加时间：2013-04-30 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料
CELSTRAN PA6-GF60-03 | PA6 | Glass Reinforced
Description
60% long fiber glass reinforced, heat stabilized, Nylon 6
| ISO Data | Physical properties | Value | Unit | Test Standard |
| Phys | Density | 1690 | kg/m³ | ISO 1183 |
| Mech | Tensile modulus (1mm/min) | 21000 | MPa | ISO 527-2/1A |
| Tensile stress at break (5mm/min) | 255 | MPa | ISO 527-2/1A | |
| Tensile strain at break (5mm/min) | 1.7 | % | ISO 527-2/1A | |
| Flexural modulus (23℃) | 19000 | MPa | ISO 178 | |
| Flexural strength (23℃) | 400 | MPa | ISO 178 | |
| Charpy notched impact strength @ 23℃ | 37 | kJ/m² | ISO 179/1eA |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.18%
CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30°C. The time between drying and processing should be as short as possible.
Note: Material can be over dried and may discolor.
Drying time (h)：2-4
Drying temperature (℃)：70-80