PA6 8233G HS BK-106 半结晶,抗紫外线
添加时间:2013-08-26 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
Ultramid® PA6 8233G HS BK-106
聚酰胺6
玻璃纤维增强材料,33%
BASF Corporation
产品说明
Ultramid 8233G HS BK-106 is a heat stabilized, weather resistant, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. This balance of engineering properties in combination with excellent processability make it ideal in applications replacing metal, resulting in an overall cost and weight savings.
Applications
Ultramid 8233G HS BK-106 is generally recommended for applications such as weed trimmer components, gears, automotive window hardware, electrical connectors and coil bobbins and all external parts exposed to the environment.
黄卡下载:E36632-231130
含添加剂:热稳定剂
填料增强:含33%玻璃纤维增强材料
材料特点:尺寸稳定,低粘度,刚性高,高强度,耐气候影响,可加工性良好,表面光洁度佳,抗热老化,抗蠕变,流动性好,耐化学,耐磨蚀,热稳定
材料用途:齿轮,连接器,汽车领域的应用,汽车外部零件,室外应用,线轴
外观颜色:黑色
外观形式:颗粒料
加工方法:注射成型
塑料牌号:PA6 8233G HS BK-106
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
物料数据
物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
比重 | 1.39 | -- | g/cm3 | ASTM D792,ISO 1183 |
收缩率 - 流动(3.18 mm) | 0.30 | -- | % | |
吸水率 | ||||
24 hr | 1.1 | -- | % | ASTM D570 |
23℃,24 hr | 1.1 | -- | % | ISO 62 |
饱和 | 6.4 | -- | % | ASTM D570 |
饱和,23℃ | 6.4 | -- | % | ISO 62 |
平衡,50% RH | 1.8 | -- | % | ASTM D570 |
平衡,23℃,50% RH | 1.8 | -- | % | ISO 62 |
硬度 | 干燥 | 调节后的 | 单位制 | 测试方法 |
洛氏硬度(R 级) | 121 | -- | ASTM D785 | |
机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
拉伸模量 | ISO 527-2 | |||
-40℃ | 10400 | 11500 | MPa | |
23℃ | 10500 | 7700 | MPa | |
80℃ | 4660 | 4600 | MPa | |
121℃ | 4020 | 4200 | MPa | |
抗张强度 | ||||
断裂,-40℃ | 210 | 215 | MPa | ASTM D638,ISO 527-2 |
断裂,23℃ | 160 | 100 | MPa | ASTM D638 |
断裂,80℃ | 85.0 | 70.0 | MPa | ASTM D638,ISO 527-2 |
断裂,121℃ | 70.0 | 60.0 | MPa | ASTM D638,ISO 527-2 |
断裂,23℃ | 155 | 100 | MPa | ISO 527-2 |
伸长率 | ||||
断裂,-40℃ | 3.0 | 2.5 | % | ASTM D638 |
断裂,23℃ | 2.0 | 6.0 | % | ASTM D638,ISO 527-2 |
断裂,80℃ | 7.0 | 6.5 | % | ASTM D638 |
断裂,121℃ | 7.0 | 6.5 | % | ASTM D638 |
弯曲模量 | ||||
23℃ | 8990 | -- | MPa | ASTM D790 |
23℃ | 8700 | -- | MPa | ISO 178 |
弯曲强度 | ||||
23℃ | 280 | -- | MPa | ASTM D790 |
23℃ | 225 | -- | MPa | ISO 178 |
冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
简支梁缺口冲击强度 | ISO 179 | |||
-30℃ | 5.5 | -- | kJ/m2 | |
23℃ | 8.0 | -- | kJ/m2 | |
简支梁无缺口冲击强度(23℃) | 55 | -- | kJ/m2 | ISO 179 |
悬壁梁缺口冲击强度 | ||||
23℃ | 110 | -- | J/m | ASTM D256 |
-40℃ | 6.0 | -- | kJ/m2 | ISO 180 |
23℃ | 8.5 | -- | kJ/m2 | ISO 180 |
热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
载荷下热变形温度 | ||||
0.45 MPa,未退火 | 218 | -- | ℃ | ASTM D648 |
0.45 MPa,未退火 | 215 | -- | ℃ | ISO 75-2/B |
1.8 MPa,未退火 | 208 | -- | ℃ | ASTM D648 |
1.8 MPa,未退火 | 205 | -- | ℃ | ISO 75-2/A |
熔融峰值温度 | 220 | -- | ℃ | ASTM D3418,ISO 3146 |
线形热膨胀系数 - 流动 | 3.8E-5 | -- | cm/cm/℃ | ASTM E831 |
电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
体积电阻率 | ||||
1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
-- | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
补充信息 | 干燥 | 调节后的 | 单位制 | 测试方法 |
Drop Weight Impact Strength(23℃) | 4.07 | -- | J | 内部方法 |
注射 | 干燥 | 单位制 | ||
干燥温度 | 83.0 | ℃ | ||
干燥时间 | 2.0 到 4.0 | hr | ||
建议的最大水分含量 | 0.15 | % | ||
加工(熔体)温度 | 270 到 295 | ℃ | ||
模具温度 | 80.0 到 95.0 | ℃ | ||
注塑压力 | 3.50 到 12.5 | MPa | ||
注射速度 | 快速 |