PA6 8253 抗冲击

添加时间:2013-08-26  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料
Ultramid PA6 8253
Ultramid® PA6 8253
聚酰胺6
BASF Corporation
 
产品说明
Ultramid 8253 is an unreinforced, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications. It is also available in heat stabilized (Ultramid 8253 HS) and/or pigmented versions. Copolymerization results in improved dry as molded toughness and increased flexibility to meet higher impact performance compared to conventional unreinforced homopolymers. Good nylon thermal and chemical properties are maintained along with good strength and stiffness retention.
 
Applications
Ultramid 8253 is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips, fasteners, flanges, key housings as well as many flexible tubing applications.
 
黄卡下载:E36632-231134
含添加剂:冲击改性剂
材料特点:改良抗撞击性,刚性好,高强度,共聚物,流动性好,柔韧性好,耐化学,韧性良好
材料用途:保护性遮盖物,草坪和园林设备,插头,电气元件,管件,紧固件,外壳
外观颜色:可用颜色,自然色
外观形式:颗粒料
加工方法:注射成型,挤出
塑料牌号:PA6 8253
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 干燥 调节后的 单位制 测试方法
比重 1.09 -- g/cm³ ASTM D792,ISO 1183
收缩率 - 流动(3.18 mm) 1.2 -- %  
吸水率        
24 hr 1.5 -- % ASTM D570
23℃,24 hr 1.5 -- % ISO 62
饱和 8.1 -- % ASTM D570
饱和,23℃ 8.1 -- % ISO 62
平衡,50% RH 2.3 -- % ASTM D570
平衡,23℃,50% RH 2.3 -- % ISO 62
硬度 干燥 调节后的 单位制 测试方法
洛氏硬度(R 级) 82 --   ASTM D785
机械性能 干燥 调节后的 单位制 测试方法
拉伸模量       ISO 527-2
-40℃ 2840 3300 MPa
23℃ 2300 730 MPa
80℃ 400 370 MPa
121℃ 295 220 MPa
抗张强度        
屈服,-40℃ 117 116 MPa ASTM D638,ISO 527-2
屈服,23℃ 65.0 32.0 MPa ASTM D638
屈服,80℃ 25.0 20.0 MPa ASTM D638,ISO 527-2
屈服,121℃ 20.0 -- MPa ASTM D638,ISO 527-2
屈服,23℃ 60.0 32.0 MPa ISO 527-2
断裂,-40℃ 100 70.0 MPa ASTM D638
断裂,23℃ 60.0 -- MPa ASTM D638
伸长率        
屈服,-40℃ 7.0 -- % ASTM D638
屈服,23℃ 4.0 15 % ASTM D638,ISO 527-2
屈服,80℃ 29 -- % ASTM D638
屈服,121℃ 34 30 % ASTM D638
断裂,-40℃ 9.0 20 % ASTM D638
断裂,23℃ > 100 > 100 % ASTM D638
标称拉伸断裂应变(23℃) 40 > 50 % ISO 527-2
弯曲模量        
-40℃ 3050 3150 MPa ASTM D790
23℃ 2210 670 MPa ASTM D790
65℃ 415 -- MPa ASTM D790
90℃ 325 -- MPa ASTM D790
121℃ 260 -- MPa ASTM D790
23℃ 1900 -- MPa ISO 178
弯曲强度        
-40℃ 148 141 MPa ASTM D790
23℃ 87.0 32.0 MPa ASTM D790
65℃ 25.0 -- MPa ASTM D790
90℃ 20.0 -- MPa ASTM D790
121℃ 14.0 -- MPa ASTM D790
23℃ 65.0 -- MPa ISO 178
冲击性能 干燥 调节后的 单位制 测试方法
简支梁缺口冲击强度       ISO 179
-30℃ 5.0 -- kJ/m²
23℃ 18 -- kJ/m²
简支梁无缺口冲击强度(23℃) 无断裂 --   ISO 179
悬壁梁缺口冲击强度       ASTM D256
-40℃ 80 64 J/m
23℃ 150J/m 无断裂  
Drop Impact Resistance(23℃) 271 -- J 内部方法
热性能 干燥 调节后的 单位制 测试方法
载荷下热变形温度        
0.45 MPa,未退火 168 -- ASTM D648
1.8 MPa,未退火 60.0 -- ASTM D648
1.8 MPa,未退火 55.0 -- ISO 75-2/A
熔融峰值温度 220 -- ASTM D3418,ISO 3146
线形热膨胀系数        
流动 9.9E-5 -- cm/cm/℃ ASTM E831
流动 8.8E-5 -- cm/cm/℃
横向 9.3E-5 -- cm/cm/℃
RTI Elec       UL 746
0.710 mm 105 --
0.750 mm 105 --
1.50 mm 105 --
3.00 mm 105 --
6.00 mm 105 --
RTI Imp       UL 746
1.50 mm 75.0 --
3.00 mm 75.0 --
6.00 mm 75.0 --
RTI       UL 746
1.50 mm 85.0 --
3.00 mm 85.0 --
6.00 mm 85.0 --
电气性能 干燥 调节后的 单位制 测试方法
体积电阻率        
1.50 mm > 1.0E+13 -- ohms·cm ASTM D257
-- > 1.0E+13 -- ohms·cm IEC 60093
漏电起痕指数 600 -- V IEC 60112
可燃性 干燥 调节后的 单位制 测试方法
UL 阻燃等级       UL 94
0.750 mm HB --  
1.50 mm HB --  
3.00 mm HB --  
6.00 mm HB --  
注射 干燥 单位制
干燥温度 80.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.20 %
加工(熔体)温度 240 到 270
模具温度 60.0 到 85.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速  
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.