PA6 8267G HS BK-106 含玻纤和矿纤增强

添加时间:2013-08-27  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料
Ultramid PA6 8267G HS BK-106
Ultramid® PA6 8267G HS BK-106
聚酰胺6
玻璃纤维增强材料,15%; 矿物填料,25%
BASF Corporation
 
产品说明
Ultramid 8267G HS BK-106 is a heat stabilized, weather resistant, 40% mineral and glass fiber reinforced PA6 injection molding compound with improved UV resistance and sink mark resistance. The combination of mineral and glass fibers result in a high performance, low warp and cost effective engineering thermoplastic. It exhibits high strength, good UV resistance, rigidity and good heat distortion temperatures. It has a relatively high resistance to creep under load. The heat stabilizer system extends its retention of properties at elevated temperatures. It has good chemical resistance to greases, oils and hydrocarbons.
 
Applications
Ultramid 8267G HS BK-106 is generally recommended for applications such as rotors, wheels, rims, timing belt covers, automotive cooling fans, shrouds and all external parts exposed to the environment.
 
填料增强:含15%玻璃纤维增强,含25%矿物填料
含添加剂:热稳定剂
材料特点:半结晶,尺寸稳定,低翘曲,低粘度,刚性好,高强度,抗弯曲,抗紫外线,可加工性好,表面光洁度佳,抗热老化,抗蠕变,流动性好,耐化学,耐磨蚀,热稳定
材料用途:把手,车轮,汽车领域的应用,室外应用
外观颜色:黑色
外观形式:颗粒料
加工方法:注射成型
塑料牌号:PA6 8267G HS BK-106
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 额定值 单位制 测试方法
比重 1.48 g/cm³ ASTM D792,ISO 1183
收缩率 - 流动(3.18 mm) 0.40 %  
吸水率      
24 hr 0.90 % ASTM D570
23℃,24 hr 0.90 % ISO 62
饱和 5.7 % ASTM D570
饱和,23℃ 5.7 % ISO 62
平衡,50% RH 1.6 % ASTM D570
平衡,23℃,50% RH 1.6 % ISO 62
硬度 额定值 单位制 测试方法
洛氏硬度(R 级) 121   ASTM D785
机械性能 额定值 单位制 测试方法
拉伸模量     ISO 527-2
-40℃ 10800 MPa
23℃ 9200 MPa
80℃ 3090 MPa
121℃ 2620 MPa
抗张强度      
断裂,-40℃ 178 MPa ASTM D638,ISO 527-2
断裂,23℃ 125 MPa ASTM D638
断裂,80℃ 59.0 MPa ASTM D638,ISO 527-2
断裂,121℃ 51.0 MPa ASTM D638,ISO 527-2
断裂,23℃ 115 MPa ISO 527-2
伸长率      
断裂,-40℃ 3.0 % ASTM D638
断裂,23℃ 2.0 % ASTM D638,ISO 527-2
断裂,80℃ 13 % ASTM D638
断裂,121℃ 11 % ASTM D638
弯曲模量      
23℃ 7580 MPa ASTM D790
23℃ 7200 MPa ISO 178
弯曲强度      
23℃ 200 MPa ASTM D790
23℃ 178 MPa ISO 178
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 5.5 kJ/m² ISO 179
简支梁无缺口冲击强度(23℃) 46 kJ/m² ISO 179
悬壁梁缺口冲击强度      
23℃ 55 J/m ASTM D256
-40℃ 4.0 kJ/m² ISO 180
23℃ 6.0 kJ/m² ISO 180
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 215 ISO 75-2/B
1.8 MPa,未退火 202 ASTM D648
1.8 MPa,未退火 200 ISO 75-2/A
熔融峰值温度 220 ASTM D3418,ISO 3146
线形热膨胀系数 - 流动 3.1E-5 cm/cm/℃ ASTM E831
注射 额定值 单位制
干燥温度 83.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.15 %
加工(熔体)温度 270 到 295
模具温度 80.0 到 95.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速  

Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.