PA6 8272G HS BK-102 含12%玻纤,热稳定

添加时间:2013-08-28  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料
Ultramid
Ultramid® PA6 8272G HS BK-102
聚酰胺6
玻璃纤维增强材料,12%
BASF Corporation
 
产品说明
Ultramid 8272G HS BK-102 is a 12% glass fiber reinforced, black pigmented, thermally modified, PA6 blow molding compound offering an excellent balance of engineering properties combined with the melt strength ideally suited for blow molding and other applications requiring ultra high melt viscosity. It exhibits improved strength, stiffness and creep resistance compare to standard blow molding grades. Outstanding permeability and chemical resistance to oils, hydrocarbons and most solvents are other advantages along with excellent stiffness and the ability to fabricate complex shapes for cost effective metal replacements.
 
Applications
Ultramid 8272G HS BK-102 is designed for blow molding applications requiring improved short term thermal performance as well as extrusions. It is ideal for air ducts, reservoirs and covers.
 
填料增强:含12%玻璃纤维增强材料
含添加剂:热稳定剂
材料特点:尺寸稳定,刚性好,高强度,很高的粘度,抗溶解,可加工性好,表面光洁度佳,抗热老化,抗蠕变,良好的熔体强度,耐化学,耐磨蚀,耐碳氢化合物,耐油,热稳定
产品用途:包装,汽车领域的应用,中冷系统,吹塑成型应用
颜色外观:黑色
产品形式:颗粒料
加工方法:吹塑成型,注射成型,挤出
塑料牌号:PA6 8272G HS BK-102
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 干燥 调节后的 单位制 测试方法
比重 1.22 -- g/cm³ ASTM D792,ISO 1183
收缩率 - 流动(3.18 mm) 0.30 -- %  
吸水率        
24 hr 1.4 -- % ASTM D570
23℃,24 hr 1.4 -- % ISO 62
饱和 8.3 -- % ASTM D570
饱和,23℃ 8.3 -- % ISO 62
平衡,50% RH 2.3 -- % ASTM D570
平衡,23℃,50% RH 2.3 -- % ISO 62
硬度 干燥 调节后的 单位制 测试方法
洛氏硬度(R 级) 121 --   ASTM D785
机械性能 干燥 调节后的 单位制 测试方法
拉伸模量       ISO 527-2
-40℃ 6370 6400 MPa
23℃ 5220 3100 MPa
80℃ 2100 1900 MPa
121℃ 1450 1500 MPa
抗张强度       ASTM D638,ISO 527-2
断裂,-40℃ 115 110 MPa
断裂,23℃ 110 60.0 MPa
断裂,121℃ 45.0 25.0 MPa
伸长率        
断裂,-40℃ 2.0 2.0 % ASTM D638
断裂,23℃ 3.0 -- % ASTM D638,ISO 527-2
断裂,121℃ 15 20 % ASTM D638
弯曲模量        
-40℃ 5200 5580 MPa ASTM D790
23℃ 4650 1970 MPa ASTM D790
121℃ 995 -- MPa ASTM D790
23℃ 4300 -- MPa ISO 178
弯曲强度       ASTM D790
-40℃ 200 265 MPa
23℃ 165 80.0 MPa
121℃ 50.0 -- MPa
冲击性能 干燥 调节后的 单位制 测试方法
简支梁缺口冲击强度(23℃) 7.1 -- kJ/m² ISO 179
悬壁梁缺口冲击强度        
-40℃ 40 40 J/m ASTM D256
23℃ 45 160 J/m ASTM D256
23℃ 5.9 -- kJ/m² ISO 180
热性能 干燥 调节后的 单位制 测试方法
热变形温度        
0.45 MPa,未退火 210 -- ISO 75-2/B
1.8 MPa,未退火 197 -- ASTM D648
1.8 MPa,未退火 170 -- ISO 75-2/A
熔融峰值温度 220 -- ASTM D3418,ISO 3146
线形热膨胀系数        
流动 9.7E-5 -- cm/cm/℃ ASTM E831
流动 2.8E-5 -- cm/cm/℃
横向 7.2E-5 -- cm/cm/℃
电气性能 干燥 调节后的 单位制 测试方法
体积电阻率        
1.50 mm > 1.0E+13 > 1.0E+13 ohms·cm ASTM D257
-- > 1.0E+13 > 1.0E+13 ohms·cm IEC 60093
补充信息 干燥 调节后的 单位制
Blow Molding Drying Temperature 80 --
Blow Molding Drying Time 2.0 到 4.0 -- hr
Blow Molding Melt Temperature 245 到 260 --
Blow Molding Moisture Content < 0.15 -- %
Blow Molding Mold Temperature 60 --
Blow-up Ratio 2.0:1.0 --  

Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.