PA6 8351 HS BK-106 高抗冲击,热稳定

添加时间:2013-08-28  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料
Ultramid PA6 8351 HS BK-106
 
Ultramid® PA6 8351 HS BK-106
聚酰胺6
BASF Corporation
 
产品说明
Ultramid 8351 HS BK-106 is a heat stabilized, pigmented black, impact modified type 6 nylon graft copolymer developed for injection molding applications requiring a high level of toughness combined with a moderate flexibility and faster cycles. Excellent thermal and chemical resistance properties provided by the nylon backbone. It demonstrates the highest impact performance within the Ultramid copolymer product line while maintaining an excellent balance of strength and stiffness. Excellent chemical resistance to greases, oils and hydrocarbons.
 
Ultramid 8351 HS BK-106 is generally recommended for applications such as storage bins, spray gun and power tool handles, trim clips and fasteners, wall anchors and automotive roof clips rack components.
 
UL 黄卡2E36632-231159
含添加剂:冲击调节器,热稳定剂
材料特点:改良抗撞击性,刚性好,共聚物,高抗撞击,良好的强度,耐化学性良好,高耐热,耐碳氢化合物,耐油,耐油脂,热稳定,韧性良好,生产阶段快
产品用途:把手,动力/其它工具,紧固件,汽车领域的应用
颜色外观:黑色
加工方法:注射成型
塑料牌号:PA6 8351 HS BK-106
定属记号:尼龙6
销售电话:185 5121 3137 谭经理
 
物料数据
物理性能 额定值 单位制 测试方法
比重 1.07 g/cm3 ASTM D792,ISO 1183
收缩率-流动(3.18 mm) 1.4 % No Standard
吸水率      
24 hr 1.1 % ASTM D570
23℃,24 hr 1.1 % ISO 62
饱和 6.7 % ASTM D570
饱和,23℃ 6.7 % ISO 62
平衡,50% RH 1.9 % ASTM D570
平衡,23℃,50% RH 1.9 % ISO 62
硬度 额定值 单位制 测试方法
洛氏硬度(R 计秤) 78   ASTM D785
机械性能 额定值 单位制 测试方法
拉伸模量(23℃) 1800 MPa ISO 527-2
抗张强度      
屈服,23℃ 55 MPa ASTM D638
屈服,23℃ 49 MPa ISO 527-2
拉伸应变      
屈服,23℃ 5 % ISO 527-2
断裂,23℃ >100 % ASTM D638
断张率(23℃) >50 % ISO 527-2
弯曲模量      
23℃ 1660 MPa ASTM D790
23℃ 1600 MPa ISO 178
弯曲强度      
23℃ 66 MPa ASTM D790
23℃ 55 MPa ISO 178
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度(23℃) 86 kJ/m2 ISO 179
简支梁缺口冲击强度(23℃) 无断裂   ISO 179
悬壁梁缺口冲击强度(23℃) 无断裂   ASTM D256
热性能 额定值 单位制 测试方法
热变形温度(1.8 MPa,未退火) 49 ISO 75-2/A
熔融峰值温度 220 ASTM D3418,ISO 3146
线形膨胀系数-流动 0.00011 cm/cm/℃ ASTM E831
注射 额定值 单位制
干燥温度 80
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.2 %
加工(熔体)温度 240 到 270
模具温度 80.0 到 95.0
注塑温度 3.50 到 12.5 MPa
注射速度 快速 -
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.