PA6 HPN 9233G HS BK-102 高耐热,抗冲击

添加时间:2013-09-10  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料
Ultramid PA6 HPN 9233G HS BK-102
Ultramid® PA6 HPN 9233G HS BK-102
33%玻璃纤维增强材料
聚酰胺6
BASF Corporation
 
产品说明
Ultramid HPN 9233G HS BK-102 is a heat stabilized, pigmented black, 33% glass reinforced PA6 injection molding grade resin in the High Productivity Nylon Series developed for improved cycle times while maintaining excellent properties. It exhibits high strength, rigidity and heat resistance. Surface appearance has been improved, cycle times reduced and creep resistance retained. This heat stabilizer version extends the retention of mechanical properties at elevated temperatures while maintaining excellent chemical resistance to greases, oils and hydrocarbons.
 
Ultramid HPN 9233G HS BK-102 is generally recommended for applications such as window locks, valve bodies, chair shells, door and window hardware, connectors, switch components, relay parts, terminal blocks, power tool housings, gears, chainsaws, blowers, trimmer housings and automotive housings.
 
黄卡下载:E36632-231189
填料增强:含33%玻璃纤维增强
含添加剂:抗冲击剂,热稳定剂
材料特点:高刚性,高强度,抗蠕变,耐化学,高耐热,耐碳氢化合物,耐油,热稳定,生产阶段快
材料用途:齿轮,电气元件,动力/其它工具,阀门/阀门部件,开关,连接器,汽车领域的应用,外壳
产品形式:颗粒料
加工方法:注射成型
外观颜色:黑色
塑料牌号:PA6 HPN 9233G HS BK-102
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 额定值 单位制 测试方法
比重 1.39 g/cm3 ASTM D792,ISO 1183
收缩率 - 流动(3.18 mm) 0.30 %  
吸水率      
24 hr 1.1 % ASTM D570
23℃,24 hr 1.1 % ISO 62
饱和 6.4 % ASTM D570
饱和,23℃ 6.4 % ISO 62
平衡,50% RH 1.8 % ASTM D570
平衡,23℃,50% RH 1.8 % ISO 62
硬度 额定值 单位制 测试方法
洛氏硬度(R 级) 120   ASTM D785
机械性能 额定值 单位制 测试方法
抗张强度(断裂,23℃) 175 MPa ASTM D638,ISO 527-2
伸长率(断裂,23℃) 3.0 % ASTM D638,ISO 527-2
弯曲模量      
23℃ 9380 MPa ASTM D790
23℃ 8400 MPa ISO 178
弯曲强度(23℃) 265 MPa ASTM D790
冲击性能 额定值 单位制 测试方法
悬壁梁缺口冲击强度      
23℃ 95 J/m ASTM D256
-40℃ 7.0 kJ/m2 ISO 180
23℃ 9.5 kJ/m2 ISO 180
Drop Impact Resistance(23℃) 4.61 J 内部方法
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 174 ISO 75-2/B
1.8 MPa,未退火 208 ASTM D648
1.8 MPa,未退火 54.0 ISO 75-2/A
熔融峰值温度 220 ASTM D3418,ISO 3146
线形热膨胀系数 - 流动 3.8E-5 cm/cm/℃ ASTM E831
RTI Elec     UL 746
0.710 mm 130
1.50 mm 140
3.00 mm 140
6.00 mm 140
RTI Imp     UL 746
0.710 mm 115
1.50 mm 115
3.00 mm 120
6.00 mm 120
RTI     UL 746
0.710 mm 140
1.50 mm 140
3.00 mm 140
6.00 mm 140
电气性能 额定值 单位制 测试方法
体积电阻率      
1.50 mm > 1.0E+13 ohms·cm ASTM D257
-- > 1.0E+13 ohms·cm IEC 60093
介电强度3(1.50 mm) 22 kV/mm ASTM D149
可燃性 额定值 单位制 测试方法
UL 阻燃等级     UL 94
1.50 mm HB  
3.00 mm HB  
6.00 mm HB  
注射 额定值 单位制
干燥温度 83.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.15 %
加工(熔体)温度 270 到 295
模具温度 80.0 到 95.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速  
备注:
3 方法A(短时间)
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.