PA6 SEG8 GY7716B 加40%玻纤增强,冲击改性

添加时间：2015-05-17 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料

Ultramid® SEG8 GY7716B

40%玻璃纤维增强材料

聚酰胺6

BASF Corporation

产品说明:

Ultramid SEG8 GY7716B is a 40% glass reinforced, impact modified, injection molding type 6 nylon requiring high strength, surface aesthetics, improved UV resistance, and good processability. This product has excellent surface appearance while maintaining a good balance of physical properties, such as high strength, improved toughness and chemical resistance. It features superior flow properties and is suited for gas assist parts and those requiring long lengths. It shows lower pressure, temperature and cycle time requirements than conventional grades.

Applications

Applications may include furniture, lawn and garden, and universal, but can be used wherever strength and appearance are critical requirements. Additionally, with improved UV performance, the use of this material in exterior applications may be applicable.

含添加剂：冲击改性剂

填料增强：含40%玻璃纤维增强

材料特性：冲击改性，高强度，可加工性良好，流动性高，耐化学，韧性良好，外观良好

材料用途：草坪和园林设备，家具，通用

加工方法：注射成型

代理销售：苏州希普能工程塑料 185 5121 3137 谭经理

塑料牌号：PA6 SEG8 GY7716B

产品物性：

物理性能	额定值	单位制	测试方法
密度	1.43	g/cm³	ISO 1183
溶化体积流率(MVR)(235℃/5.0 kg)	6.00	cm³/10min	ISO 1133
机械性能	额定值	单位制	测试方法
拉伸应力(断裂,23℃)	130	MPa	ISO 527-2
拉伸应变(断裂,23℃)	2.0	%	ISO 527-2
弯曲模量(23℃)	10500	MPa	ISO 178
冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度(23℃)	11	kJ/m²	ISO 179
悬壁梁缺口冲击强度(23℃)	13	kJ/m²	ISO 180
热性能	额定值	单位制	测试方法
热变形温度(1.8 MPa,未退火)	200	℃	ISO 75-2/A
溶融温度（DSC）	220	℃	ISO 3146
注射	额定值		单位制
干燥温度	80.0		℃
干燥时间	2.0 到 4.0		hr
建议的最大水分含量	0.080		%
料筒后部温度	245 到 275		℃
料筒中部温度	260 到 285		℃
料筒前部温度	270 到 295		℃
射嘴温度	270 到 295		℃
加工（熔体）温度	270 到 295		℃
模具温度	80.0 到 95.0		℃
注塑压力	3.50 到 12.5		MPa
注射速度	快速

Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.