PA6 TG7S BK-102 含34%玻纤,抗冲击,热稳定

添加时间:2013-09-11  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料
Ultramid PA6 TG7S BK-102
Ultramid® PA6 TG7S BK-102
聚酰胺6
玻璃纤维增强材料,34%
BASF Corporation
 
产品说明
Ultramid TG7S BK-102 is a 34% glass reinforced, pigmented black,heat stabilized, impact modified PA6 injection molding grade. It was developed to meet the demanding requirements of the first North American seat cushion pan/frame to bemade of an engineering plastic as opposed to metal. TG7S BK-102 exhibits improved strength,stiffness and notched impact properties over Ultramid 8333G HI.
 
Applications
Include cushion seat pan/frame and other automotive seating applications, automotive fan, power tools and trimmer components.
 
UL 黄卡2E36632-231205
填料增强:含34%玻璃纤维增强材料
含添加剂:冲击调节器,热稳定剂
材料特点:半结晶,尺寸稳定,低粘度,改良抗撞击,刚性佳,易加工,抗热老化,抗蠕变,流动性好,良好的强度,耐化学,耐磨蚀,热稳定,韧性良好
材料用途:气动应用,汽车的发动机罩下的零件,汽车内部零件,座椅
产品形式:颗粒料
外观颜色:黑色
加工方法:注射成型
塑料牌号:PA6 TG7S BK-102
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 额定值 单位制 测试方法
密度 1.38 g/cm³ ISO 1183
溶化体积流率(MVR)(235℃/5.0 kg) 6.00 cm³/10min ISO 1133
机械性能 额定值 单位制 测试方法
拉伸模量(23℃) 9500 MPa ISO 527-2
拉伸应力(断裂,23℃) 165 MPa ISO 527-2
拉伸应变(断裂,23℃) 2.5 % ISO 527-2
弯曲模量(23℃) 8400 MPa ISO 178
冲击性能 额定值 单位制 测试方法
悬壁梁缺口冲击强度     ISO 180
-40℃ 17 kJ/m²
23℃ 22 kJ/m²
热性能 额定值 单位制 测试方法
热变形温度      
0.45 MPa,未退火 220 ISO 75-2/B
1.8 MPa,未退火 208 ISO 75-2/A
溶融温度(DSC) 220 ISO 3146
注射 额定值 单位制
干燥温度 80.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.080 %
料筒后部温度 245 到 275
料筒中部温度 260 到 285
料筒前部温度 270 到 295
射嘴温度 270 到 295
加工(熔体)温度 270 到 295
模具温度 80.0 到 95.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速  
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.