PA66 10B40HS1 BK061 含40%矿物增强,热稳定
添加时间:2013-11-05 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
Minlon® 10B40HS1 BK061 | PA66-MD40 MINERAL REINFORCED NYLON RESIN
Regional Availability
North America, South and Central America
Processing
Injection Moulding
Delivery form
Pellets
Additives
Release agent
Product Text
Common features of Minlon® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness /toughness, good high temperature performance, good chemical resistance, paintability, dimensional stability and low warpage.
Grades with improved electrical and flammability properties are available within the Zytel® nylon resin product line. In addition, Minlon® nylon resin is available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses.
The good melt stability of Minlon® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
Minlon® nylon resin typically is used in demanding applications in the automotive, electrical, electronic, domestic appliances and construction industries.
Minlon® 10B40HS1 BK061 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding.
Injection molding
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80°C
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
PROCESSING
Melt temperature optimum = 295°C
Melt temperature range = 285-305°C
Mould temperature optimum = 100°C
Mould temperature range = 70-120°C
Maximum Screw tangential Speed : 0.15 m/s
Flow front speed : 100 mm/s
Hold pressure optimum : 70 MPa
Hold pressure range : 40-100 MPa
Back pressure : low
Hold pressure time : 3 s/mm
Maximum hold-up time : 12 min
PROPERTIES
Rheological properties | dry / cond | Unit | Test Standard |
Moulding shrinkage,parallel | 0.4 / * | % | ISO 294-4,2577 |
Moulding shrinkage,normal | 0.9 / * | % | ISO 294-4,2577 |
Mechanical properties | dry / cond | Unit | Test Standard |
Tensile Modulus | 10000 / - | Mpa | ISO 527-1/-2 |
Stress at break | 95 / - | Mpa | ISO 527-1/-2 |
Strain at break | 2.5 / - | % | ISO 527-1/-2 |
Flexural Modulus | 9500 / - | Mpa | ISO 178 |
Charpy notched impact strength | ISO 179/1eA | ||
23℃ | 3 / - | kj/㎡ | |
-40℃ | 2 / - | kj/㎡ | |
lzod notched impact strength | ISO 180/1A | ||
23℃ | 3.5 / - | kj/㎡ | |
-40℃ | 2.5 / - | kj/㎡ | |
Thermal properties | dry / cond | Unit | Test Standard |
Melting temperature,10℃/min | 263 / * | ℃ | ISO 11357-1/-3 |
Temp. of deflection under load,1.8 MPa | 205 / * | ℃ | ISO 75-1/-2 |
Temp. of deflection under load,0.45 MPa | 240 / * | ℃ | ISO 75-1/-2 |
Coeff. of linear therm. expansion,parallel | 36 / * | E-6/K | ISO 11359-1/-2 |
Coeff. of linear therm. expansion,normal | 66 / * | E-6/K | ISO 11359-1/-2 |
Flammability | dry / cond | Unit | Test Standard |
Burning Behav. at thickness h | HB / * | class | IEC 60695-11-10 |
Thickness tested | 0.7 / * | mm | IEC 60695-11-10 |
Other properties | dry / cond | Unit | Test Standard |
Density | 1510 / - | kg/m³ | ISO 1183 |