添加时间:2013-05-16 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
Eurostar Engineering Plastics
STARFLAM(阻燃)(PA-PP)
Starflam* PA66 AFR470X2
产品描述:Starflam PA66 AFR470X2 是一个含有阻燃剂和玻璃纤维增强的聚酰胺66树脂注塑成型。
Description:Starflam AFR470X2 is a Red Phosphorous Flame Retardant, Glass Fiber Reinforced Polyamide 66 Injection Molding Resin
产品数据表
功能 | PROPERTY (1) | UNIT | STANDARD | VALUE |
MECHANICAL | Flexural Modulus,2 mm/min | MPa | ISO 178 | 10250 |
Flexural Stress,break,2 mm/min | MPa | ISO 178 | 260 | |
Hardness,Rockwell L | - | ISO 2039-2 | 108 | |
Tensile Modulus,1 mm/min | MPa | ISO 527 | 11000 | |
Tensile Strain,break,5 mm/min | % | ISO 527 | 3 | |
Tensile Stress,break,5 mm/min | MPa | ISO 527 | 175 | |
IMPACT | Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm | kJ/m^2 | ISO 179/1eU | 70 |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | kJ/m^2 | ISO 179/1eA | 11 | |
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm | kJ/m^2 | ISO 179/1eU | 70 | |
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm | kJ/m^2 | ISO 179/1eA | 9 | |
Izod Impact,notched 80*10*4 +23℃ | kJ/m^2 | ISO 180/1A | 12 | |
Izod Impact,notched 80*10*4 -20℃ | kJ/m^2 | ISO 180/1A | 10 | |
Izod Impact,notched 80*10*4 -30℃ | kJ/m^2 | ISO 180/1A | 9 | |
Izod Impact,notched 80*10*4 -40℃ | kJ/m^2 | ISO 180/1A | 8 | |
THERMAL | Ball Pressure Test,125℃ +/- 2℃ | - | IEC 60695-10-2 | PASSES |
CTE,23℃ to 60℃,flow | 1/℃ | ISO 11359-2 | 2.10E-05 | |
CTE,23℃ to 60℃,xflow | 1/℃ | ISO 11359-2 | 1.50E-05 | |
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm | ℃ | ISO 75/Ae | 248 | |
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm | ℃ | ISO 75/Be | 255 | |
Relative Temp Index,Elec | ℃ | UL 746B | 100 | |
Relative Temp Index,Mech w/impact | ℃ | UL 746B | 95 | |
Relative Temp Index,Mech w/o impact | ℃ | UL 746B | 100 | |
Vicat Softening Temp,Rate B/120 | ℃ | ISO 306 | 245 | |
Vicat Softening Temp,Rate B/50 | ℃ | ISO 306 | 245 | |
PHYSICAL | Density | g/cm^3 | ISO 1183 | 1.43 |
Moisture Absorption (23℃ / 50% RH) | % | ISO 62 | 1.1 | |
Mold Shrinkage on Tensile Bar,flow | % | E2P Method | 0.2-0.3 | |
Water Absorption,(23℃/sat) | % | ISO 62 | 4.5 | |
FLAME CHARACTERISTICS | Glow Wire Flammability Index 960℃,passes at | mm | IEC 60695-2-12 | 2 |
Oxygen Index (LOI) | % | ISO 4589 | 28 | |
UL Recognized,94V-0 Flame Class Rating | mm | UL 94 | 0.75 | |
ELECTRICAL | Comparative Tracking Index | V | IEC 60112 | 600 |
Dielectric Strength,in oil,3.2 mm | kV/mm | IEC 60243-1 | 16 | |
Dissipation Factor,1 MHz | - | IEC 60250 | 0.0142 | |
Dissipation Factor,50/60 Hz | - | IEC 60250 | 0.0061 | |
Relative Permittivity,1 MHz | - | IEC 60250 | 3.2 | |
Relative Permittivity,50/60 Hz | - | IEC 60250 | 4.5 | |
Surface Resistivity,ROA | Ohm | IEC 60093 | >1.E+15 | |
Volume Resistivity | Ohm-cm | IEC 60093 | >1.E+15 |
PARAMETER | Setting | Unit |
Drying Temperature | 75-85 | ℃ |
Drying Time | 4-6 | hrs |
Maximum Moisture Content | 0.1 | % |
Mold Temperature | 70-90 | ℃ |
Rear-Zone 1 Temperature | 275-285 | ℃ |
Middle-Zone 2 Temperature | 275-285 | ℃ |
Front-Zone 3 Temperature | 275-285 | ℃ |
Melt Temperature | 275-285 | ℃ |