PA66 A27 E 复合用
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.12 到 1.15 | g/cm³ | ISO 1183 |
表观密度 | 0.70 | g/cm³ | ISO 60 |
吸水率 | ISO 62 | ||
饱和,23℃ | 8.5 | % | |
平衡,23℃,50% RH | 2.2 | % | |
粘数(96% H2SO4) | 142 到 158 | cm³/g | ISO 307 |
含水量 | < 0.40 | % | ISO 15512 |
相对粘度 - 1% in 96% Sulfuric Acid3 | 2.62 到 2.83 | ISO 307 | |
热性能 | 额定值 | 单位制 | 测试方法 |
溶融温度(DSC) | 260 | ℃ | ISO 3146 |
补充信息 | 额定值 | 单位制 | 测试方法 |
Black Specks | < 4.00 | mm²/kg | 内部方法 |
Pellet Shape | Round | ||
备注: 3 calculated by Huggins method |
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.