PA66 R515H 加15%玻纤增强,热稳定,润滑级
添加时间：2015-04-19 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料
Vydyne® R515H
15%玻璃纤维增强材料
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R515H is general-purpose, heat-stabilized, hydrolysis-resistant, 15% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved flow and offers superior surface appearance.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep, and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Vydyne R515H is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R515H has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.
Typical Applications/End Uses:
Vydyne R515H is successfully used in a wide range of injection molding engineering applications, including automotive clips, radiator end tanks, parts of the air-conditioning and petrol distribution system, etc. (under the hood); electrical connectors, housings, bobbins, etc.; and in industrial applications such as gears, bearing shells, covers, housings, etc.
黄卡下载：E70062-249083
填料增强：含15%玻璃纤维增强
含添加剂：热稳定剂，润滑剂
材料特性：高刚性，高强度，抗溶剂，良好的流动性，耐化学，耐汽油，耐油，耐油脂，热稳定，润滑，脱模性能良好
材料用途：齿轮，动力/其它工具，汽车的发动机罩下的零件，外壳
加工方法：注射成型
产品外观：自然色粒子
泛达销售：苏州希普能工程塑料 185 5121 3137 谭经理
塑料牌号：PA66 R515H
版权所有：http://www.xzslw.com/sujiao/pa66/vydyne/r515h.html
产品物性：
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度 | 1.24 | -- | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 垂直流动方向:23℃,2.00 mm | 1.0 | -- | % | |
| 流动方向:23℃,2.00 mm | 0.50 | -- | % | |
| 吸水率 | ISO 62 | |||
| 23℃,24 hr | 1.0 | -- | % | |
| 平衡,23℃,50% RH | 2.2 | -- | % | |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 6600 | 4000 | MPa | ISO 527-2 |
| 拉伸应力(断裂,23℃) | 120 | 80.0 | MPa | ISO 527-2 |
| 拉伸应变(断裂,23℃) | 3.0 | 13 | % | ISO 527-2 |
| 弯曲模量(23℃) | 5900 | 3250 | MPa | ISO 178 |
| 弯曲应力(23℃) | 170 | 110 | MPa | ISO 178 |
| 泊松比 | 0.40 | -- | ISO 527-2 | |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | |||
| -30℃ | 6.0 | 5.3 | kJ/m² | |
| 23℃ | 6.0 | 7.5 | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179 | |||
| -30℃ | 32 | 38 | kJ/m² | |
| 23℃ | 39 | 43 | kJ/m² | |
| 悬壁梁缺口冲击强度 | ISO 180 | |||
| -30℃ | 5.7 | 5.4 | kJ/m² | |
| 23℃ | 6.6 | 7.0 | kJ/m² | |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 热变形温度 | ||||
| 0.45 MPa,未退火 | 258 | -- | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 241 | -- | ℃ | ISO 75-2/A |
| 熔融温度 | 260 | -- | ℃ | ISO 11357-3 |
| 线形热膨胀系数 | ISO 11359-2 | |||
| 流动:23 到 55℃,2.00 mm | 3.0E-5 | -- | cm/cm/℃ | |
| 横向:23 到 55℃,2.00 mm | 1.1E-4 | -- | cm/cm/℃ | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 140 | -- | ℃ | |
| 1.50 mm | 140 | -- | ℃ | |
| 3.00 mm | 140 | -- | ℃ | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 120 | -- | ℃ | |
| 1.50 mm | 120 | -- | ℃ | |
| 3.00 mm | 120 | -- | ℃ | |
| RTI | UL 746 | |||
| 0.750 mm | 125 | -- | ℃ | |
| 1.50 mm | 140 | -- | ℃ | |
| 3.00 mm | 140 | -- | ℃ | |
| 电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 体积电阻率(0.750 mm) | 1.0E+13 | -- | ohm·cm | IEC 60093 |
| 介电强度(1.00 mm) | 20 | -- | kV/mm | IEC 60243 |
| 耐电弧性(3.00 mm) | PLC 6 | -- | ASTM D495 | |
| 漏电起痕指数(3.00 mm) | 250 到 399 | -- | V | IEC 60112 |
| 高电弧燃烧指数(HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| 高电压电弧起痕速率 (HVTR) | PLC 1 | -- | UL 746 | |
| 热丝引燃 (HWI) | UL 746 | |||
| 0.750 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 3 | -- | ||
| 3.00 mm | PLC 4 | -- | ||
| 可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| 灼热丝易燃指数 | IEC 60695-2-12 | |||
| 0.750 mm | 675 | -- | ℃ | |
| 1.50 mm | 675 | -- | ℃ | |
| 3.00 mm | 675 | -- | ℃ | |
| 热灯丝点火温度 | IEC 60695-2-13 | |||
| 0.750 mm | 700 | -- | ℃ | |
| 1.50 mm | 700 | -- | ℃ | |
| 3.00 mm | 700 | -- | ℃ | |
| 注射 | 干燥 | 单位制 | ||
| 干燥温度 | 80.0 | ℃ | ||
| 干燥时间 | 4.0 | hr | ||
| 建议的最大回制料比例 | 25 | % | ||
| 料筒后部温度 | 280 到 310 | ℃ | ||
| 料筒中部温度 | 280 到 310 | ℃ | ||
| 料筒前部温度 | 280 到 310 | ℃ | ||
| 射嘴温度 | 280 到 310 | ℃ | ||
| 加工（熔体）温度 | 285 到 305 | ℃ | ||
| 模具温度 | 65.0 到 95.0 | ℃ | ||
苏州希普能塑料代理销售原包首诺PA66材料，由于价格时常浮动网上就不一一报价，还请电话咨询价格，谢谢关照！