PA66 R525H BK0201 加25%玻纤增强,抗冻尼龙
添加时间:2015-04-26 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
Vydyne® R525H BK0201
25%玻璃纤维增强材料
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R525H BK0201 is hydrolysis-resistant, 25% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is lubricated for improved machine feed and flow.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Vydyne R525H BK0201 is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R525H BK0201 has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.
Typical Applications/End Uses:
Vydyne R525H BK0201 resin is used for under-the-hood automotive applications. Its hydrolysis-resistant properties make R525H BK0201 an excellent candidate for radiator end tank and heater core applications.
黄卡下载:E70062-249083
填料增强:含25%玻璃纤维增强
含添加剂:润滑剂,热稳定剂
材料特性:抗冻,抗溶剂,良好的流动性,耐化学,耐疲劳,耐汽油,耐水解,热稳定,润滑
材料用途:汽车的发动机罩下的零件
加工方法:注射成型
产品外观:黑色粒子
泛达销售:苏州希普能工程塑料 185 5121 3137 谭经理
塑料牌号:PA66 R525H BK0201
版权所有:http://www.xzslw.com/sujiao/pa66/vydyne/r525h-bk0201.html
产品物性:
物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
密度 | 1.32 | -- | g/cm³ | ISO 1183 |
收缩率 | ISO 294-4 | |||
垂直流动方向:23℃,2.00 mm | 0.90 | -- | % | |
流动方向:23℃,2.00 mm | 0.40 | -- | % | |
吸水率 | ISO 62 | |||
23℃,24 hr | 0.90 | -- | % | |
平衡,23℃,50% RH | 2.0 | -- | % | |
机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
拉伸模量(23℃) | 8600 | 5500 | MPa | ISO 527-2 |
拉伸应力(断裂,23℃) | 174 | 117 | MPa | ISO 527-2 |
拉伸应变(断裂,23℃) | 3.0 | 7 | % | ISO 527-2 |
弯曲模量(23℃) | 7700 | 5700 | MPa | ISO 178 |
弯曲应力(23℃) | 250 | 150 | MPa | ISO 178 |
泊松比 | 0.40 | -- | ISO 527-2 | |
冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
简支梁缺口冲击强度 | ISO 179/1eA | |||
-30℃ | 10 | 10 | kJ/m² | |
23℃ | 11 | 12 | kJ/m² | |
简支梁无缺口冲击强度 | ISO 179/1eU | |||
-30℃ | 55 | 66 | kJ/m² | |
23℃ | 65 | 67 | kJ/m² | |
悬壁梁缺口冲击强度 | ISO 180 | |||
-30℃ | 9.0 | 10 | kJ/m² | |
23℃ | 10 | 15 | kJ/m² | |
热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
热变形温度 | ||||
0.45 MPa,未退火 | 258 | -- | ℃ | ISO 75-2/B |
1.8 MPa,未退火 | 245 | -- | ℃ | ISO 75-2/A |
熔融温度 | 260 | -- | ℃ | ISO 11357-3 |
线形热膨胀系数 | ISO 11359-2 | |||
流动:23 到 55℃,2.00 mm | 2.5E-5 | -- | cm/cm/℃ | |
横向:23 到 55℃,2.00 mm | 1.1E-4 | -- | cm/cm/℃ | |
RTI Elec | UL 746 | |||
0.750 mm | 140 | -- | ℃ | |
1.50 mm | 140 | -- | ℃ | |
3.00 mm | 140 | -- | ℃ | |
RTI Imp | UL 746 | |||
0.750 mm | 120 | -- | ℃ | |
1.50 mm | 120 | -- | ℃ | |
3.00 mm | 120 | -- | ℃ | |
RTI | UL 746 | |||
0.750 mm | 125 | -- | ℃ | |
1.50 mm | 140 | -- | ℃ | |
3.00 mm | 140 | -- | ℃ | |
电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
体积电阻率(0.750 mm) | 1.0E+13 | -- | ohm·cm | IEC 60093 |
介电强度(1.00 mm) | 20 | -- | kV/mm | IEC 60243 |
耐电弧性(3.00 mm) | PLC 6 | -- | ASTM D495 | |
漏电起痕指数(3.00 mm) | 250 到 399 | -- | V | IEC 60112 |
高电弧燃烧指数(HAI) | UL 746 | |||
0.750 mm | PLC 0 | -- | ||
1.50 mm | PLC 0 | -- | ||
3.00 mm | PLC 0 | -- | ||
高电压电弧起痕速率 (HVTR) | PLC 1 | -- | UL 746 | |
热丝引燃 (HWI) | UL 746 | |||
0.750 mm | PLC 4 | -- | ||
1.50 mm | PLC 3 | -- | ||
3.00 mm | PLC 4 | -- | ||
可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
UL 阻燃等级 | UL 94 | |||
0.750 mm | HB | -- | ||
1.50 mm | HB | -- | ||
3.00 mm | HB | -- | ||
灼热丝易燃指数 | IEC 60695-2-12 | |||
0.750 mm | 675 | -- | ℃ | |
1.50 mm | 675 | -- | ℃ | |
3.00 mm | 675 | -- | ℃ | |
热灯丝点火温度 | IEC 60695-2-13 | |||
0.750 mm | 700 | -- | ℃ | |
1.50 mm | 700 | -- | ℃ | |
3.00 mm | 700 | -- | ℃ | |
补充信息 | 干燥 | 调节后的 | 测试方法 | |
Automotive Materials - (thickness d = 1mm) | + | -- | FMVSS 302 | |
注射 | 干燥 | 单位制 | ||
干燥温度 | 80.0 | ℃ | ||
干燥时间 | 4.0 | hr | ||
建议的最大回制料比例 | 25 | % | ||
料筒后部温度 | 280 到 310 | ℃ | ||
料筒中部温度 | 280 到 310 | ℃ | ||
料筒前部温度 | 280 到 310 | ℃ | ||
射嘴温度 | 280 到 310 | ℃ | ||
加工(熔体)温度 | 285 到 305 | ℃ | ||
模具温度 | 65.0 到 95.0 | ℃ |