PA66 R540 加40%玻璃纤增强,抗溶剂尼龙
添加时间：2015-04-28 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料
Vydyne® R540
40%玻璃纤维增强材料
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R540 is general-purpose, hydrolysis-resistant, 40% glass-fiber reinforced PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is also lubricated for improved flow and offers superior surface appearance.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Typical Applications/End Uses:
To come
黄卡下载：E70062-100521434
填料增强：含40%玻璃纤维增强
含添加剂：润滑剂
材料特性：抗冻，抗溶剂，良好的流动性，耐化学，耐疲劳，耐汽油，耐水解，润滑
材料用途：汽车的发动机罩下的零件
加工方法：注射成型
产品外观：自然色粒子
泛达销售：苏州希普能工程塑料 185 5121 3137 谭经理
塑料牌号：PA66 R540
版权所有：http://www.xzslw.com/sujiao/pa66/vydyne/r540.html
产品物性：
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度(23℃) | 1.46 | -- | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 垂直流动方向:23℃,2.00 mm | 0.90 | -- | % | |
| 流动方向:23℃,2.00 mm | 0.40 | -- | % | |
| 吸水率 | ISO 62 | |||
| 23℃,24 hr | 0.60 | -- | % | |
| 平衡,23℃,50% RH | 1.5 | -- | % | |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 14100 | 11100 | MPa | ISO 527-2 |
| 拉伸应力(断裂,23℃) | 220 | 165 | MPa | ISO 527-2 |
| 拉伸应变(断裂,23℃) | 3.0 | 4.0 | % | ISO 527-2 |
| 弯曲模量(23℃) | 12300 | 9300 | MPa | ISO 178 |
| 弯曲应力(23℃) | 335 | 250 | MPa | ISO 178 |
| 泊松比 | 0.40 | -- | ISO 527 | |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | |||
| -30℃ | 12 | 11 | kJ/m² | |
| 23℃ | 12 | 19 | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179 | |||
| -30℃ | 80 | 87 | kJ/m² | |
| 23℃ | 90 | 92 | kJ/m² | |
| 悬壁梁缺口冲击强度 | ISO 180 | |||
| -30℃ | 13 | 13 | kJ/m² | |
| 23℃ | 14 | 19 | kJ/m² | |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 热变形温度 | ||||
| 0.45 MPa,未退火 | 260 | -- | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 252 | -- | ℃ | ISO 75-2/A |
| 熔融温度 | 260 | -- | ℃ | ISO 11357-3 |
| 线形热膨胀系数 | ISO 11359-2 | |||
| 流动:23 到 55℃,2.00 mm | 1.7E-5 | -- | cm/cm/℃ | |
| 横向:23 到 55℃,2.00 mm | 1.0E-4 | -- | cm/cm/℃ | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 120 | -- | ℃ | |
| 1.50 mm | 120 | -- | ℃ | |
| 3.00 mm | 120 | -- | ℃ | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 85.0 | -- | ℃ | |
| 1.50 mm | 85.0 | -- | ℃ | |
| 3.00 mm | 105 | -- | ℃ | |
| RTI | UL 746 | |||
| 0.750 mm | 115 | -- | ℃ | |
| 1.50 mm | 120 | -- | ℃ | |
| 3.00 mm | 120 | -- | ℃ | |
| 电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 体积电阻率(3.00 mm) | 1.0E+13 | -- | ohm·cm | IEC 60093 |
| 介电强度(1.00 mm) | 24 | -- | kV/mm | IEC 60243 |
| 耐电弧性(3.00 mm) | PLC 5 | -- | ASTM D495 | |
| 漏电起痕指数(3.00 mm) | 600 | -- | V | IEC 60112 |
| 高电弧燃烧指数(HAI) | UL 746 | |||
| 0.750 mm | PLC 0 | -- | ||
| 1.50 mm | PLC 0 | -- | ||
| 3.00 mm | PLC 0 | -- | ||
| 高电压电弧起痕速率 (HVTR) | PLC 1 | -- | UL 746 | |
| 热丝引燃 (HWI) | UL 746 | |||
| 0.750 mm | PLC 4 | -- | ||
| 1.50 mm | PLC 4 | -- | ||
| 3.00 mm | PLC 4 | -- | ||
| 可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| 注射 | 干燥 | 单位制 | ||
| 干燥温度 | 80.0 | ℃ | ||
| 干燥时间 | 4.0 | hr | ||
| 建议的最大回制料比例 | 25 | % | ||
| 料筒后部温度 | 280 到 310 | ℃ | ||
| 料筒中部温度 | 280 到 310 | ℃ | ||
| 料筒前部温度 | 280 到 310 | ℃ | ||
| 射嘴温度 | 280 到 310 | ℃ | ||
| 加工（熔体）温度 | 285 到 305 | ℃ | ||
| 模具温度 | 65.0 到 95.0 | ℃ | ||