PA66/6 R633 加33%玻璃纤增强,金属取代
添加时间:2015-04-29 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
Vydyne® R633
33%玻璃纤维增强材料
聚酰胺66/6共聚物
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R633 is 33% glass-fiber reinforced, PA66/6 copolymer resin for superior surface appearance. Available in natural, this injection-molding grade resin is lubricated for machine feed and mold release.
Vydyne R633 has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption, and part weight are key advantages of Vydyne glass-reinforced PA66/6 resins over aluminum and/or zinc die-cast parts.
Typical Applications/End Uses:
Vydyne R633 has been used for many under-the-hood automotive applications, motor housings for power tools, and garden appliances. These resins have also been used in miscellaneous brackets, gears and clips that require high rigidity and strength.
填料增强:含33%玻璃纤维增强
含添加剂:润滑剂
材料特性:高刚性,高拉伸强度,高强度,共聚物,润滑,脱模性能良好,优良外观
材料用途:草坪和园林设备,齿轮,动力/其它工具,金属取代,外壳
加工方法:注射成型
产品外观:自然色粒子
泛达销售:苏州希普能工程塑料 185 5121 3137 谭经理
塑料牌号:PA66/6 R633
版权所有:http://www.xzslw.com/sujiao/pa66/vydyne/r633.html
产品物性:
物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
密度 | 1.39 | -- | g/cm³ | ISO 1183 |
收缩率 | ISO 294-4 | |||
垂直流动方向:23℃,2.00 mm | 0.90 | -- | % | |
流动方向:23℃,2.00 mm | 0.40 | -- | % | |
吸水率 | ISO 62 | |||
23℃,24 hr | 1.3 | -- | % | |
平衡,23℃,50% RH | 2.3 | -- | % | |
机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
拉伸模量(23℃) | 10800 | 8000 | MPa | ISO 527-2 |
拉伸应力(断裂,23℃) | 184 | 130 | MPa | ISO 527-2 |
拉伸应变(断裂,23℃) | 4.0 | 6.0 | % | ISO 527-2 |
弯曲模量(23℃) | 8800 | 6800 | MPa | ISO 178 |
弯曲应力(23℃) | 255 | 195 | MPa | ISO 178 |
泊松比 | 0.40 | -- | ISO 527-2 | |
冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
简支梁缺口冲击强度 | ISO 179 | |||
-30℃ | 11 | 15 | kJ/m² | |
23℃ | 12 | 25 | kJ/m² | |
简支梁无缺口冲击强度 | ISO 179 | |||
-30℃ | 44 | 91 | kJ/m² | |
23℃ | 51 | 92 | kJ/m² | |
悬壁梁缺口冲击强度 | ISO 180 | |||
-30℃ | 12 | 19 | kJ/m² | |
23℃ | 13 | 22 | kJ/m² | |
热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
热变形温度 | ||||
0.45 MPa,未退火 | 230 | -- | ℃ | ISO 75-2/B |
1.8 MPa,未退火 | 220 | -- | ℃ | ISO 75-2/A |
熔融温度 | 233 | -- | ℃ | ISO 11357-3 |
线形热膨胀系数 | ISO 11359-2 | |||
流动:23 到 55℃,2.00 mm | 1.5E-5 | -- | cm/cm/℃ | |
横向:23 到 55℃,2.00 mm | 1.0E-4 | -- | cm/cm/℃ | |
注射 | 干燥 | 单位制 | ||
干燥温度 | 80.0 | ℃ | ||
干燥时间 | 4.0 | hr | ||
建议的最大回制料比例 | 25 | % | ||
料筒后部温度 | 280 到 310 | ℃ | ||
料筒中部温度 | 280 到 310 | ℃ | ||
料筒前部温度 | 280 到 310 | ℃ | ||
射嘴温度 | 280 到 310 | ℃ | ||
加工(熔体)温度 | 285 到 305 | ℃ | ||
模具温度 | 65.0 到 95.0 | ℃ |