PA66 79G13HSL NC010 含13%玻纤,热稳定,耐冲击

添加时间:2013-11-19  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料

DuPont PA66 79G13HSL NC010

Zytel® 79G13HSL NC010 | PA66-I-GF13 NYLON RESIN
 
Regional Availability
Europe, Near East/Africa
 
Processing
Injection Moulding
 
Delivery form
Pellets
 
Additives
Lubricants
 
Special characteristics
Heat stabilised or stable to heat
 
Product Text
ISO 1874-PA66-MGH,14-050,GF13
 
Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured.
 
The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
 
Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
 
Zytel® 79G13HSL NC010 is a 13 % glass reinforced, heat stabilised, lubricated slightly toughened black polyamide 66 for injection moulding. It has improved impact resistance.
 
Injection molding
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80℃
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
 
PROCESSING
Melt temperature optimum = 295℃
Melt temperature range = 285-305℃
 
PROPERTIES
Rheological properties dry / cond Unit Test Standard
Moulding shrinkage,parallel 0.5 / * % ISO 294-4,2577
Moulding shrinkage,normal 0.8 / * % ISO 294-4,2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 5100 / 3700 MPa ISO 527-1/-2
Stress at break 118 / 67 MPa ISO 527-1/-2
Strain at break 4 / 10 % ISO 527-1/-2
Tensile creep modulus,1h * / 4030 MPa ISO 899-1
Tensile creep modulus,1000h * / 3180 MPa ISO 899-1
Charpy impact strength,23℃ 67 / 59 kJ/m² ISO 179/1eU
Charpy impact strength,-30℃ 59 / 54 kJ/m² ISO 179/1eU
Charpy notched impact strength,23℃ 8 / 14 kJ/m² ISO 179/1eA
Charpy notched impact strength,-30℃ 6 / 6 kJ/m² ISO 179/1eA
Thermal properties dry / cond Unit Test Standard
Melting temperature,10℃/min 263 / * ISO 11357-1/-3
Temp. of deflection under load,1.8 MPa 242 / * ISO 75-1/-2
Temp. of deflection under load,0.45 MPa 260 / * ISO 75-1/-2
Vicat softening temperature,50℃/h,50N 239 / * ISO 306
Coeff. of linear therm. expansion,parallel 50 / * E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion,normal 130 / * E-6/K ISO 11359-1/-2
Flammability dry / cond Unit Test Standard
Burning Behav. at 1.5 mm nom. thickn. HB / * class IEC 60695-11-10
Thickness tested 1.5 / * mm IEC 60695-11-10
UL recognition UL / * - -
Burning Behav. at thickness h HB / * class IEC 60695-11-10
Thickness tested 0.8 / * mm IEC 60695-11-10
Electrical properties dry / cond Unit Test Standard
Comparative tracking index 250 / - - IEC 60112
Other properties dry / cond Unit Test Standard
Water absorption,2mm 6.5 / * % Sim. to ISO 62
Humidity absorption,2mm 2.2 / * % Sim. to ISO 62
Density 1210 / - kg/m³ ISO 1183
Material specific properties dry / cond Unit Test Standard
Viscosity number 150 / * cm³/g ISO 307,1157,1628
Rheological calc. properties Value Unit Test Standard
Density of melt 1040 kg/m³ -
Min. mould temperature 40 -
Max. mould temperature 90 -
Min. melt temperature 285 -
Max. melt temperature 305 -
VDA Properties Value Unit Test Standard
Odour 4[1] class VDA 270
1:C3      