PA66 E53 NC010 高粘度,挤出级
添加时间:2013-11-20 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
Zytel® E53 NC010 | PA66 NYLON RESIN
Regional Availability
Europe, Near East/Africa
Processing
Film Extrusion, Profile Extrusion, Sheet Extrusion, Other Extrusion, Coatable, Casting
Delivery form
Pellets
Product Text
Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured.
The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
Zytel® E53 NC010 is a very high viscosity polyamide 66 resin for extrusion.
Profile extrusion
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80℃
Drying time, dehumidified dryer = 4-6 h
Processing moisture content = <0.05 %
PROCESSING
Melt temperature optimum = 285℃
Melt temperature range = 280-290℃
PROPERTIES
Rheological properties | dry / cond | Unit | Test Standard |
Moulding shrinkage,parallel | 1.6 / * | % | ISO 294-4,2577 |
Mechanical properties | dry / cond | Unit | Test Standard |
Tensile Modulus | 3000 / 1200 | MPa | ISO 527-1/-2 |
Yield stress | 84 / 55 | MPa | ISO 527-1/-2 |
Yield strain | 4.4 / 30 | % | ISO 527-1/-2 |
Nominal strain at break | >50 / >50 | % | ISO 527-1/-2 |
Charpy impact strength,23℃ | N / - | kJ/m² | ISO 179/1eU |
Charpy notched impact strength,23℃ | 7 / 40 | kJ/m² | ISO 179/1eA |
Charpy notched impact strength,-30℃ | 6 / 4 | kJ/m² | ISO 179/1eA |
Thermal properties | dry / cond | Unit | Test Standard |
Melting temperature,10℃/min | 263 / * | ℃ | ISO 11357-1/-3 |
Temp. of deflection under load,1.8 MPa | 74 / * | ℃ | ISO 75-1/-2 |
Temp. of deflection under load,0.45 MPa | 205 / * | ℃ | ISO 75-1/-2 |
Coeff. of linear therm. expansion,parallel | 100 / * | E-6/K | ISO 11359-1/-2 |
Coeff. of linear therm. expansion,normal | 100 / * | E-6/K | ISO 11359-1/-2 |
Electrical properties | dry / cond | Unit | Test Standard |
Relative permittivity,100Hz | 3.9 / - | - | IEC 60250 |
Volume resistivity | 1E11 / - | Ohm*m | IEC 60093 |
Other properties | dry / cond | Unit | Test Standard |
Water absorption,2mm | 8.5 / * | % | Sim. to ISO 62 |
Humidity absorption,2mm | 2.7 / * | % | Sim. to ISO 62 |
Density | 1140 / - | kg/m³ | ISO 1183 |
Material specific properties | dry / cond | Unit | Test Standard |
Viscosity number | 350 / * | cm³/g | ISO 307,1157,1628 |
VDA Properties | Value | Unit | Test Standard |
Burning rate,Thickness 1 mm | 0[1] | mm/min | ISO 3795 (FMVSS 302) |
1:DNI |