PA66 FG53 NC010 高粘度,食品级

添加时间:2013-11-21  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料

DuPont PA66 FG53 NC010

Zytel® FG53 NC010 | PA66 NYLON RESIN
 
Regional Availability
North America, Europe, South and Central America, Near East/Africa
 
Processing
Film Extrusion, Profile Extrusion, Sheet Extrusion, Other Extrusion, Coatable, Casting
 
Delivery form
Pellets
 
Product Text
Zytel® FG50 is an unreinforced, very high viscosity polyamide 66 for extrusion. It has been developed for consideration into applications such as parts for the food industry.
 
FOOD CONTACT
This product is manufactured according to Good Manufacturing Practice (GMP) principles and generally accepted in food contact applications in Europe and the USA when meeting applicable use conditions. For details, individual compliance statements are available from your DuPont representative
 
Profile extrusion
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80℃
Drying time, dehumidified dryer = 4-6 h
Processing moisture content = <0.05 %
 
PROCESSING
Melt temperature optimum = 285℃
Melt temperature range = 280-290℃
 
PROPERTIES
Rheological properties dry / cond Unit Test Standard
Moulding shrinkage,parallel 1.6 / * % ISO 294-4,2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 3000 / 1200 MPa ISO 527-1/-2
Yield stress 84 / 55 MPa ISO 527-1/-2
Yield strain 4.4 / 30 % ISO 527-1/-2
Nominal strain at break >50 / >50 % ISO 527-1/-2
Charpy impact strength,23℃ N / - kJ/m² ISO 179/1eU
Charpy notched impact strength,23℃ 7 / 40 kJ/m² ISO 179/1eA
Charpy notched impact strength,-30℃ 6 / 4 kJ/m² ISO 179/1eA
Thermal properties dry / cond Unit Test Standard
Melting temperature,10℃/min 263 / * ISO 11357-1/-3
Temp. of deflection under load,1.8 MPa 74 / * ISO 75-1/-2
Temp. of deflection under load,0.45 MPa 205 / * ISO 75-1/-2
Coeff. of linear therm. expansion,parallel 100 / * E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion,normal 100 / * E-6/K ISO 11359-1/-2
Electrical properties dry / cond Unit Test Standard
Relative permittivity,100Hz 3.9 / - - IEC 60250
Volume resistivity 1E11 / - Ohm*m IEC 60093
Other properties dry / cond Unit Test Standard
Water absorption,2mm 8.5 / * % Sim. to ISO 62
Humidity absorption,2mm 2.7 / * % Sim. to ISO 62
Density 1140 / - kg/m³ ISO 1183
Material specific properties dry / cond Unit Test Standard
Viscosity number 350 / * cm³/g ISO 307,1157,1628

 

Chemical Media Resistance

Acids

√ Acetic Acid (5% by mass) (23℃)

√ Citric Acid solution (10% by mass) (23℃)

√ Lactic Acid (10% by mass) (23℃)

× Hydrochloric Acid (36% by mass) (23℃)

× Nitric Acid (40% by mass) (23℃)

× Sulfuric Acid (38% by mass) (23℃)

× Sulfuric Acid (5% by mass) (23℃)

× Chromic Acid solution (40% by mass) (23℃)

Bases

× Sodium Hydroxide solution (35% by mass) (23℃)

√ Sodium Hydroxide solution (1% by mass) (23℃)

√ Ammonium Hydroxide solution (10% by mass) (23℃)

Alcohols

√ Isopropyl alcohol (23℃)

√ Methanol (23℃)

√ Ethanol (23℃)

Hydrocarbons

√ n-Hexane (23℃)

√ Toluene (23℃)

√ iso-Octane (23℃)

Ketones

√ Acetone (23℃)

Ethers

√ Diethyl ether (23℃)

Mineral oils

√ SAE 10W40 multigrade motor oil (23℃)

× SAE 10W40 multigrade motor oil (130℃)

× SAE 80/90 hypoid-gear oil (130℃)

√ Insulating Oil (23℃)

Standard Fuels

√ ISO 1817 Liquid 1 (60℃)

√ ISO 1817 Liquid 2 (60℃)

√ ISO 1817 Liquid 3 (60℃)

√ ISO 1817 Liquid 4 (60℃)

√ Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23℃)

√ Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23℃)

√ Diesel fuel (pref. ISO 1817 Liquid F) (23℃)

√ Diesel fuel (pref. ISO 1817 Liquid F) (90℃)

× Diesel fuel (pref. ISO 1817 Liquid F) (>90℃)

Salt solutions

√ Sodium Chloride solution (10% by mass) (23℃)

× Sodium Hypochlorite solution (10% by mass) (23℃)

√ Sodium Carbonate solution (20% by mass) (23℃)

√ Sodium Carbonate solution (2% by mass) (23℃)

× Zinc Chloride solution (50% by mass) (23℃)

Other

√ Ethyl Acetate (23℃)

× Hydrogen peroxide (23℃)

× DOT No. 4 Brake fluid (130℃)

× Ethylene Glycol (50% by mass) in water (108℃)

√ 1% nonylphenoxy-polyethyleneoxy ethanol in water (23℃)

√ 50% Oleic acid + 50% Olive Oil (23℃)

√ Water (23℃)

× Water (90℃)

× Phenol solution (5% by mass) (23℃)

 

Symbols used:

√ possibly resistant

Defined as: Supplier has sufficient indication that contact with chemical can be potentially accepted under the intended use conditions and expected service life. Criteria for assessment have to be indicated (e.g. surface aspect, volume change, property change).

 

× not recommended - see explanation

Defined as: Not recommended for general use. However, short-term exposure under certain restricted conditions could be acceptable (e.g. fast cleaning with thorough rinsing, spills, wiping, vapor exposure).