PBT HR5330HFS NC010 含30%玻纤,抗水解
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.50 | g/cm3 | ISO 1183 |
溶化体积流率(MVR)(250℃/2.16 kg) | 7.50 | cm3/10min | ISO 1133 |
收缩率 | ISO 294-4 | ||
垂直流动方向 | 1.0 | % | |
流动方向 | 0.30 | % | |
吸水率 | ISO 62 | ||
23℃,24 hr,2.00 mm | 0.35 | % | |
平衡,23℃,2.00 mm,50% RH | 0.15 | % | |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 8500 | MPa | ISO 527-2 |
拉伸应力(断裂) | 130 | MPa | ISO 527-2 |
拉伸应变(断裂) | 3.1 | % | ISO 527-2 |
弯曲应力 | 195 | MPa | ISO 178 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 | ISO 179/1eA | ||
-40℃ | 10 | kJ/m2 | |
23℃ | 13 | kJ/m2 | |
简支梁无缺口冲击强度(23℃) | 70 | kJ/m2 | ISO 179/1eU |
热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 | |||
0.45 MPa,未退火 | 222 | ℃ | ISO 75-2/B |
1.8 MPa,未退火 | 207 | ℃ | ISO 75-2/A |
玻璃转化温度2 | 65.0 | ℃ | ISO 11357-2 |
熔融温度2 | 225 | ℃ | ISO 11357-3 |
电气性能 | 额定值 | 单位制 | 测试方法 |
表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
体积电阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
介电强度 | 34 | kV/mm | IEC 60243-1 |
漏电起痕指数 | 575 | V | IEC 60112 |
可燃性 | 额定值 | 单位制 | 测试方法 |
燃烧速率(1.00 mm) | 30 | mm/min | ISO 3795 |
可燃性等级(1.50 mm) | HB | IEC 60695-11-10,-20 | |
极限氧指数 | 20 | % | ISO 4589-2 |
充模分析 | 额定值 | 单位制 | 测试方法 |
熔体粘度(250℃,1000 sec^-1) | 230 | Pa·s | ISO 11443 |
备注: 2 10℃/min |
Rheological properties | Value | Unit | Test Standard |
Moulding shrinkage,parallel | 0.3 | % | ISO 294-4,2577 |
Moulding shrinkage,normal | 1 | % | ISO 294-4,2577 |
Mechanical properties | Value | Unit | Test Standard |
Tensile Modulus | 8400 | MPa | ISO 527-1/-2 |
Stress at break | 130 | MPa | ISO 527-1/-2 |
Strain at break | 3.1 | % | ISO 527-1/-2 |
Charpy impact strength,23℃ | 70 | kJ/m² | ISO 179/1eU |
Charpy notched impact strength,23℃ | 13 | kJ/m² | ISO 179/1eA |
Thermal properties | Value | Unit | Test Standard |
Melting temperature,10℃/min | 225 | ℃ | ISO 11357-1/-3 |
Glass transition temperature,10℃/min | 65 | ℃ | ISO 11357-1/-2 |
Temp. of deflection under load,1.8 MPa | 207 | ℃ | ISO 75-1/-2 |
Temp. of deflection under load,0.45 MPa | 222 | ℃ | ISO 75-1/-2 |
Flammability | Value | Unit | Test Standard |
Burning Behav. at 1.5 mm nom. thickn. | HB | class | IEC 60695-11-10 |
Thickness tested | 1.5 | mm | IEC 60695-11-10 |
Oxygen index | 20 | % | ISO 4589-1/-2 |
Electrical properties | Value | Unit | Test Standard |
Volume resistivity | >1E13 | Ohm*m | IEC 60093 |
Comparative tracking index | 600 | - | IEC 60112 |
Other properties | Value | Unit | Test Standard |
Water absorption,2mm | 0.35 | % | Sim. to ISO 62 |
Humidity absorption,2mm | 0.15 | % | Sim. to ISO 62 |
Density | 1500 | kg/m³ | ISO 1183 |
Rheological calc. properties | Value | Unit | Test Standard |
Min. mould temperature | 30 | ℃ | - |
Max. mould temperature | 140 | ℃ | - |
Min. melt temperature | 240 | ℃ | - |
Max. melt temperature | 260 | ℃ | - |
VDA Properties | Value | Unit | Test Standard |
Burning rate,Thickness 1 mm | 30 | mm/min | ISO 3795 (FMVSS 302) |
Chemical Media Resistance
Acids
√ Acetic Acid (5% by mass) (23℃)
√ Citric Acid solution (10% by mass) (23℃)
√ Lactic Acid (10% by mass) (23℃)
× Hydrochloric Acid (36% by mass) (23℃)
× Nitric Acid (40% by mass) (23℃)
× Sulfuric Acid (38% by mass) (23℃)
× Sulfuric Acid (5% by mass) (23℃)
× Chromic Acid solution (40% by mass) (23℃)
Bases
× Sodium Hydroxide solution (35% by mass) (23℃)
√ Sodium Hydroxide solution (1% by mass) (23℃)
√ Ammonium Hydroxide solution (10% by mass) (23℃)
Alcohols
√ Isopropyl alcohol (23℃)
√ Methanol (23℃)
√ Ethanol (23℃)
Hydrocarbons
√ n-Hexane (23℃)
√ Toluene (23℃)
√ iso-Octane (23℃)
Ketones
√ Acetone (23℃)
Ethers
√ Diethyl ether (23℃)
Mineral oils
√ SAE 10W40 multigrade motor oil (23℃)
× SAE 10W40 multigrade motor oil (130℃)
× SAE 80/90 hypoid-gear oil (130℃)
√ Insulating Oil (23℃)
Standard Fuels
× ISO 1817 Liquid 1 (60℃)
× ISO 1817 Liquid 2 (60℃)
× ISO 1817 Liquid 3 (60℃)
× ISO 1817 Liquid 4 (60℃)
√ Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23℃)
√ Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23℃)
√ Diesel fuel (pref. ISO 1817 Liquid F) (23℃)
√ Diesel fuel (pref. ISO 1817 Liquid F) (90℃)
× Diesel fuel (pref. ISO 1817 Liquid F) (>90℃)
Salt solutions
√ Sodium Chloride solution (10% by mass) (23℃)
√ Sodium Hypochlorite solution (10% by mass) (23℃)
√ Sodium Carbonate solution (20% by mass) (23℃)
√ Sodium Carbonate solution (2% by mass) (23℃)
√ Zinc Chloride solution (50% by mass) (23℃)
Other
√ Ethyl Acetate (23℃)
× Hydrogen peroxide (23℃)
× DOT No. 4 Brake fluid (130℃)
× Ethylene Glycol (50% by mass) in water (108℃)
√ 1% nonylphenoxy-polyethyleneoxy ethanol in water (23℃)
√ 50% Oleic acid + 50% Olive Oil (23℃)
√ Water (23℃)
× Water (90℃)
√ Phenol solution (5% by mass) (23℃)
Symbols used:
√ possibly resistant
Defined as: Supplier has sufficient indication that contact with chemical can be potentially accepted under the intended use conditions and expected service life. Criteria for assessment have to be indicated (e.g. surface aspect, volume change, property change).
× not recommended - see explanation
Defined as: Not recommended for general use. However, short-term exposure under certain restricted conditions could be acceptable (e.g. fast cleaning with thorough rinsing, spills, wiping, vapor exposure).