PBT 176 Resin 纯PBT树脂纤维
添加时间:2014-05-21 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
VALOX™ PBT 176 Resin
非增强型
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Americas)
产品说明
Unreinforced, neat PBT resin for fibers. Natural Color Only, Not intended for injection molding.
材料颜色:自然色
定属记号:PBT
塑料牌号:PBT 176
加工方法:挤出复合
销售电话:185 5121 3137 谭经理
销售地址:http://www.xzslw.com/sujiao/pbt/valox/176.html
材料物性
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,50 mm/min | 500 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,50 mm/min | 500 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,50 mm/min | 2 | % | ASTM D 638 |
Tensile Strain,brk,Type I,50 mm/min | 2 | % | ASTM D 638 |
Tensile Modulus,5 mm/min | 25400 | kgf/cm² | ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span | 850 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3 mm/min,50 mm span | 24300 | kgf/cm² | ASTM D 790 |
Tensile Stress,yield,50 mm/min | 45 | MPa | ISO 527 |
Tensile Stress,break,50 mm/min | 45 | MPa | ISO 527 |
Tensile Strain,yield,50 mm/min | 1.8 | % | ISO 527 |
Tensile Strain,break,50 mm/min | 1.8 | % | ISO 527 |
Tensile Modulus,1 mm/min | 2600 | MPa | ISO 527 |
Flexural Stress,yield,2 mm/min | 81 | MPa | ISO 178 |
Flexural Modulus,2 mm/min | 2290 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 90 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 2 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Total Energy,23℃ | 50 | cm-kgf | ASTM D 3763 |
Izod Impact,unnotched 80*10*4 +23℃ | 35 | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 2 | kJ/m² | ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
HDT,0.45 MPa,3.2 mm,unannealed | 104 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 48 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 8.5E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 8.5E-05 | 1/℃ | ISO 11359-2 |
Vicat Softening Temp,Rate B/50 | 178 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 177 | ℃ | ISO 306 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 113 | ℃ | ISO 75/Bf |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 51 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.32 | - | ASTM D 792 |
Mold Shrinkage,flow,3.2 mm(5) | 1.5-1.8 | % | SABIC Method |
Mold Shrinkage,xflow,3.2 mm(5) | 1.6-2 | % | SABIC Method |
Melt Flow Rate,250℃/1.2 kgf | 127 | g/10 min | ASTM D 1238 |
Melt Viscosity | 350 | poise | SABIC Method |
Density | 1.31 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 0.08 | % | ISO 62 |
Moisture Absorption(23℃/50% RH) | 0.07 | % | ISO 62 |
Melt Volume Rate,MVR at 250℃/1.2 kg | 127 | cm³/10 min | ISO 1133 |
Melt Volume Rate,MVR at 250℃/2.16 kg | 231 | cm³/10 min | ISO 1133 |
Compounding Extrusion | Value | Unit | |
Drying Temperature | 110-120 | ℃ | |
Drying Time | 4-6 | hrs | |
Drying Time(Cumulative) | 8 | hrs | |
Maximum Moisture Content | 0 | % | |
Melt Temperature | 245-260 | ℃ | |
Barrel-Zone 1 Temperature | 200-230 | ℃ | |
Barrel-Zone 2 Temperature | 240-255 | ℃ | |
Barrel-Zone 3 Temperature | 240-275 | ℃ | |
Barrel-Zone 4 Temperature | 240-275 | ℃ | |
Adapter Temperature | 240-275 | ℃ | |
Die Temperature | 240-275 | ℃ | |
Waterbath Temperature | 25-35 | ℃ |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.