VALOX™ PBT 311 Resin
非增强型
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Americas)
产品说明
Unreinforced, improved resistance to UV. Medium viscosity.
材料特点:抗紫外线改进,中等粘度
定属记号:PBT
塑料牌号:PBT 311
销售电话:185 5121 3137 谭经理
销售地址:http://www.xzslw.com/sujiao/pbt/valox/311.html
材料物性
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,50 mm/min | 520 | kgf/cm² | ASTM D 638 |
Tensile Strain,brk,Type I,50 mm/min | 300 | % | ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span | 840 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3 mm/min,50 mm span | 23900 | kgf/cm² | ASTM D 790 |
Hardness,Rockwell R | 117 | - | ASTM D 785 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 163 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
Modified Gardner,23℃ | 414 | cm-kgf | ASTM D 3029 |
THERMAL | Value | Unit | Standard |
HDT,0.45 MPa,6.4 mm,unannealed | 154 | ℃ | ASTM D 648 |
HDT,1.82 MPa,6.4 mm,unannealed | 54 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 8.1E-05 | 1/℃ | ASTM E 831 |
CTE,60℃ to 138℃,flow | 1.39E-04 | 1/℃ | ASTM E 831 |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.31 | - | ASTM D 792 |
Specific Volume | 0.76 | cm³/g | ASTM D 792 |
Water Absorption,24 hours | 0.08 | % | ASTM D 570 |
Mold Shrinkage,flow,0.75-2.3 mm(5) | 0.9-1.6 | % | SABIC Method |
Mold Shrinkage,flow,2.3-4.6 mm(5) | 1.5-2.3 | % | SABIC Method |
Mold Shrinkage,xflow,0.75-2.3 mm(5) | 1-1.7 | % | SABIC Method |
Mold Shrinkage,xflow,2.3-4.6 mm(5) | 1.6-2.4 | % | SABIC Method |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | >4.E+16 | Ohm-cm | ASTM D 257 |
Dielectric Strength,in air,3.2 mm | 15.7 | kV/mm | ASTM D 149 |
Dielectric Strength,in oil,1.6 mm | 23.2 | kV/mm | ASTM D 149 |
Relative Permittivity,100 Hz | 3.3 | - | ASTM D 150 |
Relative Permittivity,1 MHz | 3.1 | - | ASTM D 150 |
Dissipation Factor,100 Hz | 0.002 | - | ASTM D 150 |
Dissipation Factor,1 MHz | 0.02 | - | ASTM D 150 |
Injection Molding | Value | Unit | |
Drying Temperature | 120 | ℃ | |
Drying Time | 3-4 | hrs | |
Drying Time(Cumulative) | 12 | hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 245-260 | ℃ | |
Nozzle Temperature | 240-255 | ℃ | |
Front-Zone 3 Temperature | 245-260 | ℃ | |
Middle-Zone 2 Temperature | 240-255 | ℃ | |
Rear-Zone 1 Temperature | 230-250 | ℃ | |
Mold Temperature | 50-75 | ℃ | |
Back Pressure | 0.3-0.7 | MPa | |
Screw Speed | 50-100 | rpm | |
Shot to Cylinder Size | 40-80 | % | |
Vent Depth | 0.013-0.025 | mm |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.