PBT 780 Resin 阻燃级
添加时间:2014-06-15 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
VALOX™ PBT 780 Resin
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Americas)
产品说明
40% gl/min, UL94 V-0 rated. Nonblooming flame retardant. Circuit breaker handles/housings, motor coil housings.
材料特点:阻燃UL94 V-0
材料用途:断路器手柄/外壳,电机线圈外壳
定属记号:PBT
塑料牌号:PBT 780
销售电话:185 5121 3137 谭经理
销售地址:http://www.xzslw.com/sujiao/pbt/valox/780.html
材料物性
MECHANICAL | Value | Unit | Standard |
Tensile Stress,brk,Type I,5 mm/min | 1010 | kgf/cm² | ASTM D 638 |
Flexural Stress,brk,1.3 mm/min,50 mm span | 1680 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3 mm/min,50 mm span | 105400 | kgf/cm² | ASTM D 790 |
Hardness,Rockwell R | 116 | - | ASTM D 785 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched,23℃ | 38 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
THERMAL | Value | Unit | Standard |
HDT,0.45 MPa,6.4 mm,unannealed | 210 | ℃ | ASTM D 648 |
HDT,1.82 MPa,6.4 mm,unannealed | 193 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 2.52E-05 | 1/℃ | ASTM E 831 |
CTE,60℃ to 138℃,flow | 2.88E-05 | 1/℃ | ASTM E 831 |
Relative Temp Index,Elec | 130 | ℃ | UL 746B |
Relative Temp Index,Mech w/impact | 130 | ℃ | UL 746B |
Relative Temp Index,Mech w/o impact | 140 | ℃ | UL 746B |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.77 | - | ASTM D 792 |
Specific Volume | 0.56 | cm³/g | ASTM D 792 |
Water Absorption,24 hours | 0.02 | % | ASTM D 570 |
Mold Shrinkage,flow,1.5-3.2 mm(5) | 0.3-0.4 | % | SABIC Method |
Mold Shrinkage,flow,3.2-4.6 mm(5) | 0.4-0.6 | % | SABIC Method |
Mold Shrinkage,xflow,1.5-3.2 mm(5) | 0.4-0.6 | % | SABIC Method |
Mold Shrinkage,xflow,3.2-4.6 mm(5) | 0.6-0.8 | % | SABIC Method |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | 3.5E+15 | Ohm-cm | ASTM D 257 |
Dielectric Strength,in air,3.2 mm | 18.1 | kV/mm | ASTM D 149 |
Dielectric Strength,in oil,1.6 mm | 25.5 | kV/mm | ASTM D 149 |
Relative Permittivity,100 Hz | 3.9 | - | ASTM D 150 |
Relative Permittivity,1 MHz | 3.8 | - | ASTM D 150 |
Dissipation Factor,100 Hz | 0.007 | - | ASTM D 150 |
Dissipation Factor,1 MHz | 0.02 | - | ASTM D 150 |
Arc Resistance,Tungsten{PLC} | 6 | PLC Code | ASTM D 495 |
Hot Wire Ignition{PLC) | 1 | PLC Code | UL 746A |
High Voltage Arc Track Rate{PLC} | 1 | PLC Code | UL 746A |
High Ampere Arc Ign,surface{PLC} | 4 | PLC Code | UL 746A |
Comparative Tracking Index(UL){PLC} | 3 | PLC Code | UL 746A |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Recognized,94V-0 Flame Class Rating(3) | 0.81 | mm | UL 94 |
Injection Molding | Value | Unit | |
Drying Temperature | 120 | ℃ | |
Drying Time | 3-4 | hrs | |
Drying Time(Cumulative) | 12 | hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 255-275 | ℃ | |
Nozzle Temperature | 255-270 | ℃ | |
Front-Zone 3 Temperature | 255-265 | ℃ | |
Middle-Zone 2 Temperature | 250-260 | ℃ | |
Rear-Zone 1 Temperature | 245-255 | ℃ | |
Mold Temperature | 65-95 | ℃ | |
Back Pressure | 0.3-0.7 | MPa | |
Screw Speed | 50-80 | rpm | |
Shot to Cylinder Size | 40-80 | % | |
Vent Depth | 0.025-0.038 | mm |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.