VALOX™ PBT HX215HP Resin
非增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Americas)
产品说明
High Flow, Unreinforced, Polybutylene Terephthalate (PBT) with mold release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. Available in limited colors.
含添加剂:脱模剂
材料特点:高流动
材料用途:应用于医疗器械和制药领域
定属记号:PBT
塑料牌号:PBT HX215HP
销售电话:185 5121 3137 谭经理
销售地址:http://www.xzslw.com/sujiao/pbt/valox/hx215hp.html
材料物性
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,50 mm/min | 610 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,50 mm/min | 260 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,50 mm/min | 3.7 | % | ASTM D 638 |
Tensile Strain,brk,Type I,50 mm/min | 10 | % | ASTM D 638 |
Tensile Modulus,5 mm/min | 27500 | kgf/cm² | ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span | 900 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3 mm/min,50 mm span | 25400 | kgf/cm² | ASTM D 790 |
Tensile Stress,yield,50 mm/min | 50 | MPa | ISO 527 |
Tensile Stress,break,50 mm/min | 49 | MPa | ISO 527 |
Tensile Strain,yield,50 mm/min | 3.2 | % | ISO 527 |
Tensile Strain,break,50 mm/min | 10 | % | ISO 527 |
Tensile Modulus,1 mm/min | 2600 | MPa | ISO 527 |
Flexural Stress,yield,2 mm/min | 80 | MPa | ISO 178 |
Flexural Modulus,2 mm/min | 2260 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,notched,23℃ | 3 | cm-kgf/cm | ASTM D 256 |
Izod Impact,notched,-30℃ | 3 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Total Energy,23℃ | 203 | cm-kgf | ASTM D 3763 |
Izod Impact,notched 80*10*4 +23℃ | 2 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 -30℃ | 2 | kJ/m² | ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m² | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp,Rate B/50 | 180 | ℃ | ASTM D 1525 |
HDT,0.45 MPa,3.2 mm,unannealed | 150 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 54 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 7.6E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 7.8E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,flow | 7.6E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 7.8E-05 | 1/℃ | ISO 11359-2 |
Vicat Softening Temp,Rate B/50 | 183 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 180 | ℃ | ISO 306 |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 49 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.31 | - | ASTM D 792 |
Mold Shrinkage,flow,3.2 mm(5) | 1.5-2 | % | SABIC Method |
Melt Flow Rate,250℃/2.16 kgf | 80 | g/10 min | ASTM D 1238 |
Density | 1.31 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 0.34 | % | ISO 62 |
Moisture Absorption(23℃/50% RH) | 0.08 | % | ISO 62 |
Melt Volume Rate,MVR at 250℃/2.16 kg | 70 | cm³/10 min | ISO 1133 |
Injection Molding | Value | Unit | |
Drying Temperature | 120 | ℃ | |
Drying Time | 3-4 | hrs | |
Drying Time(Cumulative) | 12 | hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 245-260 | ℃ | |
Nozzle Temperature | 240-255 | ℃ | |
Front-Zone 3 Temperature | 245-260 | ℃ | |
Middle-Zone 2 Temperature | 240-255 | ℃ | |
Rear-Zone 1 Temperature | 230-250 | ℃ | |
Mold Temperature | 50-75 | ℃ | |
Back Pressure | 0.3-0.7 | MPa | |
Screw Speed | 50-100 | rpm | |
Shot to Cylinder Size | 40-80 | % | |
Vent Depth | 0.013-0.025 | mm | |
Compounding Extrusion | Value | Unit | |
Drying Temperature | 110-120 | ℃ | |
Drying Time | 4-6 | hrs | |
Drying Time(Cumulative) | 8 | hrs | |
Maximum Moisture Content | 0 | % | |
Melt Temperature | 245-260 | ℃ | |
Barrel-Zone 1 Temperature | 200-230 | ℃ | |
Barrel-Zone 2 Temperature | 240-255 | ℃ | |
Barrel-Zone 3 Temperature | 240-275 | ℃ | |
Barrel-Zone 4 Temperature | 240-275 | ℃ | |
Adapter Temperature | 240-275 | ℃ | |
Die Temperature | 240-275 | ℃ | |
Waterbath Temperature | 25-35 | ℃ |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.