添加时间:2014-06-22 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
VALOX™ PBT HX3061HP Resin
非增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Americas)
产品说明
PBT for compounding/fibers only. Not intended for injection molding. Biocompatible. Melt viscosity: 250C at 21.6 kgf is 1450-1850 poise. Available in Natural color (1001) only.
材料特点:熔体粘度:250℃/21.6公斤
材料用途:仅适用于复合/纤维
定属记号:PBT
塑料牌号:PBT HX3061HP
加工方法:挤出复合
销售电话:185 5121 3137 谭经理
销售地址:http://www.xzslw.com/sujiao/pbt/valox/hx3061hp.html
材料物性
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,50 mm/min | 590 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,50 mm/min | 260 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,50 mm/min | 3.7 | % | ASTM D 638 |
Tensile Strain,brk,Type I,50 mm/min | 140 | % | ASTM D 638 |
Tensile Modulus,5 mm/min | 26500 | kgf/cm² | ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span | 840 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3 mm/min,50 mm span | 24400 | kgf/cm² | ASTM D 790 |
Tensile Stress,yield,50 mm/min | 50 | MPa | ISO 527 |
Tensile Stress,break,50 mm/min | 49 | MPa | ISO 527 |
Tensile Strain,yield,50 mm/min | 3.2 | % | ISO 527 |
Tensile Strain,break,50 mm/min | 8.6 | % | ISO 527 |
Tensile Modulus,1 mm/min | 2600 | MPa | ISO 527 |
Flexural Stress,yield,2 mm/min | 80 | MPa | ISO 178 |
Flexural Modulus,2 mm/min | 2200 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,notched,23℃ | 3 | cm-kgf/cm | ASTM D 256 |
Izod Impact,notched,-30℃ | 3 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Total Energy,23℃ | 254 | cm-kgf | ASTM D 3763 |
Izod Impact,notched 80*10*4 +23℃ | 4 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 -30℃ | 3 | kJ/m² | ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp,Rate B/50 | 167 | ℃ | ASTM D 1525 |
HDT,0.45 MPa,3.2 mm,unannealed | 120 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 49 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 7.6E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 7.8E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,flow | 7.6E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 7.8E-05 | 1/℃ | ISO 11359-2 |
Vicat Softening Temp,Rate B/50 | 173 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 169 | ℃ | ISO 306 |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 49 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.31 | - | ASTM D 792 |
Mold Shrinkage,flow,3.2 mm (5) | 1.5-2 | % | SABIC Method |
Mold Shrinkage,xflow,3.2 mm (5) | 1.5-2 | % | SABIC Method |
Melt Flow Rate,250℃/2.16 kgf | 50 | g/10 min | ASTM D 1238 |
Melt Viscosity | 1650 | poise | SABIC Method |
Density | 1.31 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 0.34 | % | ISO 62 |
Moisture Absorption (23℃ / 50% RH) | 0.08 | % | ISO 62 |
Melt Volume Rate,MVR at 250℃/2.16 kg | 45 | cm³/10 min | ISO 1133 |
Compounding Extrusion | Value | Unit | |
Drying Temperature | 110-120 | ℃ | |
Drying Time | 4-6 | hrs | |
Drying Time (Cumulative) | 8 | hrs | |
Maximum Moisture Content | 0 | % | |
Melt Temperature | 245-260 | ℃ | |
Barrel-Zone 1 Temperature | 200-230 | ℃ | |
Barrel-Zone 2 Temperature | 240-255 | ℃ | |
Barrel-Zone 3 Temperature | 240-275 | ℃ | |
Barrel-Zone 4 Temperature | 240-275 | ℃ | |
Adapter Temperature | 240-275 | ℃ | |
Die Temperature | 240-275 | ℃ | |
Waterbath Temperature | 25-35 | ℃ |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.