添加时间：2014-04-30 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料
VALOX™ PBT K4530 Resin
15%玻璃纤维增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
15% glass reinforced PBT, Hydrolytically stable, High flow, Automotive connectors.
增强填料：含15%玻纤增强
材料特点：抗水解稳定,高流动
材料用途：汽车连接器
定属记号：PBT
塑料牌号：PBT K4530
加工方法：注射成型
销售电话：185 5121 3137 谭经理
销售地址：http://www.xzslw.com/sujiao/pbt/valox/k4530-resin.html
材料物性
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5 mm/min | 1050 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5 mm/min | 1050 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5 mm/min | 4 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5 mm/min | 4 | % | ASTM D 638 |
| Tensile Modulus,5 mm/min | 36200 | kgf/cm² | ASTM D 638 |
| Flexural Stress,brk,1.3 mm/min,50 mm span | 1520 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3 mm/min,50 mm span | 47300 | kgf/cm² | ASTM D 790 |
| Tensile Stress,yield,5 mm/min | 98 | MPa | ISO 527 |
| Tensile Stress,break,5 mm/min | 98 | MPa | ISO 527 |
| Tensile Strain,yield,5 mm/min | 3.1 | % | ISO 527 |
| Tensile Strain,break,5 mm/min | 3.1 | % | ISO 527 |
| Tensile Modulus,1 mm/min | 5250 | MPa | ISO 527 |
| Flexural Stress,yield,2 mm/min | 150 | MPa | ISO 178 |
| Flexural Stress,break,2 mm/min | 150 | MPa | ISO 178 |
| Flexural Modulus,2 mm/min | 4750 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact,unnotched,23℃ | 40 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,unnotched 80*10*4 +23℃ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 7 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT,0.45 MPa,3.2 mm,unannealed | 218 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 193 | ℃ | ASTM D 648 |
| Vicat Softening Temp,Rate B/120 | 205 | ℃ | ISO 306 |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.41 | - | ASTM D 792 |
| Mold Shrinkage,flow,3.2 mm(5) | 0.7-0.9 | % | SABIC Method |
| Mold Shrinkage,xflow,3.2 mm(5) | 1-1.2 | % | SABIC Method |
| Melt Volume Rate,MVR at 250℃/2.16 kg | 17 | cm³/10 min | ISO 1133 |
| AFTER 40 CYCLES,SIMILAR TO USCAR-2,CLASS III | Value | Unit | Standard |
| Tensile Stress,brk,Type I,5 mm/min | 830 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,5 mm/min | 2.5 | % | ASTM D 638 |
| Flexural Modulus,1.3 mm/min,50 mm span | 46100 | kgf/cm² | ASTM D 790 |
| Flexural Strain,1.3 mm/min,50 mm span | 9.7 | % | ASTM D 790 |
| Instrumented Impact,Total Energy,23℃ | 60 | cm-kgf | ASTM D 3763 |
| PROPERTIES AFTER 1008 HOURS AT 125?C | Value | Unit | Standard |
| Tensile Stress,brk,Type I,5 mm/min | 990 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,5 mm/min | 4 | % | ASTM D 638 |
| Flexural Modulus,1.3 mm/min,50 mm span | 49100 | kgf/cm² | ASTM D 790 |
| Flexural Strain,1.3 mm/min,50 mm span | 7 | % | ASTM D 790 |
| Instrumented Impact,Total Energy,23℃ | 50 | cm-kgf | ASTM D 3763 |
| AFTER 40 CYCLES,SIMILAR TO USCAR-2,CLASS IV | Value | Unit | Standard |
| Tensile Stress,brk,Type I,5 mm/min | 910 | kgf/cm² | ASTM D 638 |
| Tensile Strain,brk,Type I,5 mm/min | 2.3 | % | ASTM D 638 |
| Flexural Modulus,1.3 mm/min,50 mm span | 52000 | kgf/cm² | ASTM D 790 |
| Flexural Strain,1.3 mm/min,50 mm span | 6 | % | ASTM D 790 |
| Instrumented Impact,Total Energy,23℃ | 50 | cm-kgf | ASTM D 3763 |
| PROPERTIES AFTER 1008 HOURS AT 155?C | Value | Unit | Standard |
| Tensile Stress,brk,Type I,5 mm/min | 49070 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5 mm/min | 97.2 | % | ASTM D 638 |
| Flexural Modulus,1.3 mm/min,50 mm span | 0 | kgf/cm² | ASTM D 790 |
| Flexural Strain,1.3 mm/min,50 mm span | 3.8 | % | ASTM D 790 |
| Injection Molding | Value | Unit | |
| Drying Temperature | 60-75 | ℃ | |
| Drying Time | 4-6 | hrs | |
| Drying Time(Cumulative) | 8 | hrs | |
| Maximum Moisture Content | 0.05 | % | |
| Melt Temperature | 250-265 | ℃ | |
| Nozzle Temperature | 245-260 | ℃ | |
| Front-Zone 3 Temperature | 250-265 | ℃ | |
| Middle-Zone 2 Temperature | 245-260 | ℃ | |
| Rear-Zone 1 Temperature | 240-255 | ℃ | |
| Mold Temperature | 65-90 | ℃ | |
| Back Pressure | 0.3-0.7 | MPa | |
| Screw Speed | 50-80 | rpm | |
| Shot to Cylinder Size | 40-80 | % | |
| Vent Depth | 0.025-0.038 | mm | |
• We cannot overemphasize -- OVERDRYING SHOULD BE AVOIDED. Use a dehumidifying desiccant bed dryer with -30℃ (-20℉) dew point air (approximately 1 cfm/lb/hr air flow). Exceeding the temperature or time recommended can compromise the hydrolysis performance of the material or the drying equipment can be damaged.
• If material is stored in dryer for extended periods (overnight or more):
Lower dryer temperature to room temperature.
Recirculate cool dry air over material.
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.