添加时间:2014-05-01 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
VALOX™ PBT SHF4340 Resin
20%玻璃纤维增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
20% GF Super High Flow PBT
增强填料:含20%玻纤增强
含添加剂:脱模
材料特点:超高流动
定属记号:PBT
塑料牌号:PBT SHF4340
加工方法:注射成型
销售电话:185 5121 3137 谭经理
销售地址:http://www.xzslw.com/sujiao/pbt/valox/shf4340-resin.html
材料物性
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,5 mm/min | 1070 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,5 mm/min | 1070 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,5 mm/min | 2 | % | ASTM D 638 |
Tensile Strain,brk,Type I,5 mm/min | 2 | % | ASTM D 638 |
Tensile Modulus,5 mm/min | 69300 | kgf/cm² | ASTM D 638 |
Tensile Stress,yield,5 mm/min | 110 | MPa | ISO 527 |
Tensile Stress,break,5 mm/min | 110 | MPa | ISO 527 |
Tensile Strain,yield,5 mm/min | 3 | % | ISO 527 |
Tensile Strain,break,5 mm/min | 3 | % | ISO 527 |
Tensile Modulus,1 mm/min | 6700 | MPa | ISO 527 |
Flexural Stress,yield,2 mm/min | 160 | MPa | ISO 178 |
Flexural Stress,break,2 mm/min | 160 | MPa | ISO 178 |
Flexural Strain,break,2 mm/min | 3 | % | ISO 178 |
Flexural Modulus,2 mm/min | 5600 | MPa | ISO 178 |
Hardness,H358/30 | 185 | MPa | ISO 2039-1 |
Hardness,Rockwell R | 118 | - | ISO 2039-2 |
IMPACT | Value | Unit | Standard |
Charpy Impact,unnotched,23℃ | 35 | kJ/m² | ISO 179/2C |
Charpy Impact,unnotched,-30℃ | 25 | kJ/m² | ISO 179/2C |
Izod Impact,unnotched,23℃ | 35 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,unnotched,-30℃ | 33 | cm-kgf/cm | ASTM D 4812 |
Izod Impact,notched,23℃ | 8 | cm-kgf/cm | ASTM D 256 |
Izod Impact,notched,0℃ | 8 | cm-kgf/cm | ASTM D 256 |
Izod Impact,notched,-30℃ | 8 | cm-kgf/cm | ASTM D 256 |
Izod Impact,unnotched 80*10*4 +23℃ | 30 | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 8 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 0℃ | 8 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 -30℃ | 8 | kJ/m² | ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m² | ISO 179/1eA |
Charpy Impact,notched,23℃ | 9 | kJ/m² | ISO 179/2C |
Charpy Impact,notched,-30℃ | 9 | kJ/m² | ISO 179/2C |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp,Rate A/50 | 220 | ℃ | ASTM D 1525 |
Vicat Softening Temp,Rate B/50 | 205 | ℃ | ASTM D 1525 |
HDT,0.45 MPa,3.2 mm,unannealed | 223 | ℃ | ASTM D 648 |
HDT,1.82 MPa,3.2mm,unannealed | 205 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 4.E-05 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 1.E-04 | 1/℃ | ISO 11359-2 |
Ball Pressure Test,125℃ +/- 2℃ | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp,Rate A/50 | 220 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/50 | 205 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 200 | ℃ | ISO 306 |
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 223 | ℃ | ISO 75/Bf |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 205 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.44 | - | ASTM D 792 |
Filler Content | 20 | % | ASTM D 229 |
Mold Shrinkage on Tensile Bar,flow(2)(5) | 0.3-0.7 | % | SABIC Method |
Mold Shrinkage on Tensile Bar,xflow(2)(5) | 0.4-1 | % | SABIC Method |
Density | 1.44 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 0.15 | % | ISO 62 |
Moisture Absorption(23℃/50% RH) | 0.03 | % | ISO 62 |
Melt Volume Rate,MVR at 250℃/2.16 kg | 40 | cm³/10 min | ISO 1133 |
Melt Viscosity,250℃,1500 sec-1 | 95 | Pa-s | ISO 11443 |
Melt Viscosity,260℃,1500 sec-1 | 55 | Pa-s | ISO 11443 |
ELECTRICAL | Value | Unit | Standard |
Dielectric Strength,in oil,0.8 mm | 33 | kV/mm | IEC 60243-1 |
Dielectric Strength,in oil,1.6 mm | 25.3 | kV/mm | IEC 60243-1 |
Dielectric Strength,in oil,3.2 mm | 18.6 | kV/mm | IEC 60243-1 |
Dissipation Factor,1 MHz | 0.018 | - | IEC 60250 |
Comparative Tracking Index | 375 | V | IEC 60112 |
Injection Molding | Value | Unit | |
Drying Temperature | 110-120 | ℃ | |
Drying Time | 2-4 | hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 250-270 | ℃ | |
Nozzle Temperature | 240-260 | ℃ | |
Front-Zone 3 Temperature | 245-265 | ℃ | |
Middle-Zone 2 Temperature | 240-255 | ℃ | |
Rear-Zone 1 Temperature | 230-245 | ℃ | |
Hopper Temperature | 40-60 | ℃ | |
Mold Temperature | 40-100 | ℃ |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.