添加时间:2014-05-01 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
VALOX™ PBT SHF436HR Resin
30%玻璃纤维增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
PBT, Super High Flow, 30% glass reinforced,hydrolytically resistant.
增强填料:含30%玻纤增强
材料特点:超高流动,抗水解
定属记号:PBT
塑料牌号:PBT SHF436HR
加工方法:注射成型
销售电话:185 5121 3137 谭经理
销售地址:http://www.xzslw.com/sujiao/pbt/valox/shf436hr-resin.html
材料物性
MECHANICAL | Value | Unit | Standard |
Tensile Stress,yld,Type I,5 mm/min | 1130 | kgf/cm² | ASTM D 638 |
Tensile Stress,brk,Type I,5 mm/min | 1130 | kgf/cm² | ASTM D 638 |
Tensile Strain,yld,Type I,5 mm/min | 2 | % | ASTM D 638 |
Tensile Strain,brk,Type I,5 mm/min | 2 | % | ASTM D 638 |
Tensile Modulus,5 mm/min | 121300 | kgf/cm² | ASTM D 638 |
Flexural Stress,yld,1.3 mm/min,50 mm span | 1660 | kgf/cm² | ASTM D 790 |
Flexural Modulus,1.3 mm/min,50 mm span | 88700 | kgf/cm² | ASTM D 790 |
Tensile Stress,yield,5 mm/min | 117 | MPa | ISO 527 |
Tensile Stress,break,5 mm/min | 117 | MPa | ISO 527 |
Tensile Strain,yield,5 mm/min | 2 | % | ISO 527 |
Tensile Strain,break,5 mm/min | 2 | % | ISO 527 |
Tensile Modulus,1 mm/min | 9490 | MPa | ISO 527 |
Flexural Stress,yield,2 mm/min | 165 | MPa | ISO 178 |
Flexural Modulus,2 mm/min | 7720 | MPa | ISO 178 |
IMPACT | Value | Unit | Standard |
Izod Impact,notched,23℃ | 9 | cm-kgf/cm | ASTM D 256 |
Izod Impact,notched,-30℃ | 9 | cm-kgf/cm | ASTM D 256 |
Instrumented Impact Total Energy,23℃ | 61 | cm-kgf | ASTM D 3763 |
Izod Impact,notched 80*10*4 +23℃ | 8 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 -30℃ | 8 | kJ/m² | ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 8 | kJ/m² | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp,Rate B/50 | 200 | ℃ | ASTM D 1525 |
HDT,1.82 MPa,3.2mm,unannealed | 214 | ℃ | ASTM D 648 |
CTE,-40℃ to 40℃,flow | 1.E-04 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,xflow | 3.E-05 | 1/℃ | ASTM E 831 |
CTE,-40℃ to 40℃,flow | 1.E-04 | 1/℃ | ISO 11359-2 |
CTE,-40℃ to 40℃,xflow | 3.E-05 | 1/℃ | ISO 11359-2 |
Vicat Softening Temp,Rate B/50 | 200 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 200 | ℃ | ISO 306 |
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 206 | ℃ | ISO 75/Af |
PHYSICAL | Value | Unit | Standard |
Specific Gravity | 1.53 | - | ASTM D 792 |
Mold Shrinkage,flow,3.2 mm(5) | 0.3-0.5 | % | SABIC Method |
Melt Flow Rate,250℃/2.16 kgf | 30 | g/10 min | ASTM D 1238 |
Density | 1.53 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 0.28 | % | ISO 62 |
Moisture Absorption(23℃/50% RH) | 0.06 | % | ISO 62 |
Melt Volume Rate,MVR at 250℃/2.16 kg | 30 | cm³/10 min | ISO 1133 |
Injection Molding | Value | Unit | |
Drying Temperature | 120 | ℃ | |
Drying Time | 3-4 | hrs | |
Drying Time(Cumulative) | 12 | hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 250-265 | ℃ | |
Nozzle Temperature | 245-260 | ℃ | |
Front-Zone 3 Temperature | 250-265 | ℃ | |
Middle-Zone 2 Temperature | 245-260 | ℃ | |
Rear-Zone 1 Temperature | 240-255 | ℃ | |
Mold Temperature | 65-90 | ℃ | |
Back Pressure | 0.3-0.7 | MPa | |
Screw Speed | 50-80 | rpm | |
Shot to Cylinder Size | 40-80 | % | |
Vent Depth | 0.025-0.038 | mm |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.