添加时间:2014-05-21 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
VALOX™ PBT VX3101N Resin
未增强
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
VALOX VX3101N is an unreinforced PBT injection moulding resin, with excellent flow properties, good hydrolitical stability and chemical resistance.
材料特点:高流动,抗水解稳定,抗化学良好
定属记号:PBT
塑料牌号:PBT VX3101N
加工方法:注塑
销售电话:185 5121 3137 谭经理
销售地址:http://www.xzslw.com/sujiao/pbt/valox/vx3101n.html
材料物性
MECHANICAL | Value | Unit | Standard |
Taber Abrasion,CS-17,1 kg | 9 | mg/1000cy | SABIC Method |
Tensile Stress,yield,50 mm/min | 65 | MPa | ISO 527 |
Tensile Stress,break,50 mm/min | 50 | MPa | ISO 527 |
Tensile Strain,yield,50 mm/min | 3.5 | % | ISO 527 |
Tensile Strain,break,50 mm/min | 15 | % | ISO 527 |
Tensile Modulus,1 mm/min | 2800 | MPa | ISO 527 |
Flexural Stress,yield,2 mm/min | 85 | MPa | ISO 178 |
Flexural Modulus,2 mm/min | 2600 | MPa | ISO 178 |
Hardness,H358/30 | 100 | MPa | ISO 2039-1 |
IMPACT | Value | Unit | Standard |
Izod Impact,unnotched 80*10*4 +23℃ | NB | kJ/m² | ISO 180/1U |
Izod Impact,unnotched 80*10*4 -30℃ | NB | kJ/m² | ISO 180/1U |
Izod Impact,notched 80*10*4 +23℃ | 4 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 0℃ | 2 | kJ/m² | ISO 180/1A |
Izod Impact,notched 80*10*4 -30℃ | 2 | kJ/m² | ISO 180/1A |
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m² | ISO 179/1eA |
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m² | ISO 179/1eU |
THERMAL | Value | Unit | Standard |
CTE,23℃ to 60℃,flow | 1.3E-04 | 1/℃ | ISO 11359-2 |
CTE,23℃ to 60℃,xflow | 1.3E-04 | 1/℃ | ISO 11359-2 |
Ball Pressure Test,125℃ +/- 2℃ | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp,Rate B/50 | 183 | ℃ | ISO 306 |
Vicat Softening Temp,Rate B/120 | 185 | ℃ | ISO 306 |
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm | 175 | ℃ | ISO 75/Be |
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm | 60 | ℃ | ISO 75/Ae |
PHYSICAL | Value | Unit | Standard |
Mold Shrinkage on Tensile Bar,flow(2)(5) | 1.1-1.8 | % | SABIC Method |
Mold Shrinkage on Tensile Bar,xflow(2)(5) | 0.9-1.8 | % | SABIC Method |
Density | 1.31 | g/cm³ | ISO 1183 |
Water Absorption,(23℃/sat) | 0.34 | % | ISO 62 |
Moisture Absorption(23℃/50% RH) | 0.08 | % | ISO 62 |
Melt Volume Rate,MVR at 250℃/1.2 kg | 20 | cm³/10 min | ISO 1133 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
Surface Resistivity,ROA | >1.E+15 | Ohm | IEC 60093 |
Dielectric Strength,in oil,3.2 mm | 16 | kV/mm | IEC 60243-1 |
Relative Permittivity,1 MHz | 2.9 | - | IEC 60250 |
Dissipation Factor,50/60 Hz | 0.002 | - | IEC 60250 |
Dissipation Factor,1 MHz | 0.02 | - | IEC 60250 |
Comparative Tracking Index | 600 | V | IEC 60112 |
Relative Permittivity,50/60 Hz | 3.1 | - | IEC 60250 |
FLAME CHARACTERISTICS | Value | Unit | Standard |
UL Compliant,94HB Flame Class Rating(3)(4) | 1.5 | mm | UL 94 by SABIC-IP |
Glow Wire Flammability Index 850℃,passes at | 1 | mm | IEC 60695-2-12 |
Oxygen Index(LOI) | 20 | % | ISO 4589 |
Injection Molding | Value | Unit | |
Drying Temperature | 110-120 | ℃ | |
Drying Time | 2-4 | hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 250-270 | ℃ | |
Nozzle Temperature | 240-260 | ℃ | |
Front-Zone 3 Temperature | 245-265 | ℃ | |
Middle-Zone 2 Temperature | 240-255 | ℃ | |
Rear-Zone 1 Temperature | 230-245 | ℃ | |
Hopper Temperature | 40-60 | ℃ | |
Mold Temperature | 40-100 | ℃ |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.