PBT VX4510 Resin 含10%玻纤增强,阻燃
添加时间：2014-05-21 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料
VALOX™ PBT VX4510 Resin
10%玻璃纤维
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
VALOX VX4510 is a flame retarded, 10% glassfiber reinforced injection moulding PBT resin.
增强填料：含10%玻纤增强
材料特点：阻燃V0
定属记号：PBT
塑料牌号：PBT VX4510
加工方法：注塑
销售电话：185 5121 3137 谭经理
销售地址：http://www.xzslw.com/sujiao/pbt/valox/vx4510.html
材料物性
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress,yld,Type I,5 mm/min | 880 | kgf/cm² | ASTM D 638 |
| Tensile Stress,brk,Type I,5 mm/min | 880 | kgf/cm² | ASTM D 638 |
| Tensile Strain,yld,Type I,5 mm/min | 3 | % | ASTM D 638 |
| Tensile Strain,brk,Type I,5 mm/min | 3 | % | ASTM D 638 |
| Tensile Modulus,5 mm/min | 54000 | kgf/cm² | ASTM D 638 |
| Flexural Stress,yld,1.3 mm/min,50 mm span | 1270 | kgf/cm² | ASTM D 790 |
| Flexural Stress,brk,1.3 mm/min,50 mm span | 1270 | kgf/cm² | ASTM D 790 |
| Flexural Modulus,1.3 mm/min,50 mm span | 40700 | kgf/cm² | ASTM D 790 |
| Taber Abrasion,CS-17,1 kg | 45 | mg/1000cy | SABIC Method |
| Tensile Stress,yield,5 mm/min | 90 | MPa | ISO 527 |
| Tensile Stress,break,5 mm/min | 90 | MPa | ISO 527 |
| Tensile Strain,yield,5 mm/min | 3 | % | ISO 527 |
| Tensile Strain,break,5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus,1 mm/min | 5400 | MPa | ISO 527 |
| Flexural Stress,yield,2 mm/min | 140 | MPa | ISO 178 |
| Flexural Stress,break,2 mm/min | 135 | MPa | ISO 178 |
| Flexural Strain,break,2 mm/min | 4 | % | ISO 178 |
| Flexural Modulus,2 mm/min | 4500 | MPa | ISO 178 |
| Hardness,H358/30 | 100 | MPa | ISO 2039-1 |
| Hardness,Rockwell R | 120 | - | ISO 2039-2 |
| IMPACT | Value | Unit | Standard |
| Charpy Impact,unnotched,23℃ | 33 | kJ/m² | ISO 179/2C |
| Charpy Impact,unnotched,-30℃ | 28 | kJ/m² | ISO 179/2C |
| Izod Impact,unnotched,23℃ | 40 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,unnotched,-30℃ | 32 | cm-kgf/cm | ASTM D 4812 |
| Izod Impact,notched,23℃ | 5 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,0℃ | 5 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,notched,-30℃ | 5 | cm-kgf/cm | ASTM D 256 |
| Izod Impact,unnotched 80*10*4 +23℃ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact,unnotched 80*10*4 -30℃ | 25 | kJ/m² | ISO 180/1U |
| Izod Impact,notched 80*10*4 +23℃ | 5 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 0℃ | 5 | kJ/m² | ISO 180/1A |
| Izod Impact,notched 80*10*4 -30℃ | 5 | kJ/m² | ISO 180/1A |
| Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy Impact,notched,23℃ | 6 | kJ/m² | ISO 179/2C |
| Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m² | ISO 179/1eA |
| Charpy Impact,notched,-30℃ | 6 | kJ/m² | ISO 179/2C |
| Charpy 23℃,Unnotch Edgew 80*10*4 sp=62mm | 25 | kJ/m² | ISO 179/1eU |
| Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eU |
| THERMAL | Value | Unit | Standard |
| Vicat Softening Temp,Rate A/50 | 220 | ℃ | ASTM D 1525 |
| Vicat Softening Temp,Rate B/50 | 202 | ℃ | ASTM D 1525 |
| HDT,0.45 MPa,3.2 mm,unannealed | 215 | ℃ | ASTM D 648 |
| HDT,1.82 MPa,3.2mm,unannealed | 190 | ℃ | ASTM D 648 |
| CTE,-40℃ to 40℃,flow | 4.19E-05 | 1/℃ | ISO 11359-2 |
| CTE,-40℃ to 40℃,xflow | 7.21E-05 | 1/℃ | ISO 11359-2 |
| CTE,23℃ to 80℃,flow | 5.E-05 | 1/℃ | ISO 11359-2 |
| CTE,23℃ to 80℃,xflow | 1.6E-04 | 1/℃ | ISO 11359-2 |
| CTE,23℃ to 150℃,flow | 4.55E-05 | 1/℃ | ISO 11359-2 |
| CTE,23℃ to 150℃,xflow | 1.76E-04 | 1/℃ | ISO 11359-2 |
| Ball Pressure Test,125℃ +/- 2℃ | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp,Rate A/50 | 220 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/50 | 203 | ℃ | ISO 306 |
| Vicat Softening Temp,Rate B/120 | 202 | ℃ | ISO 306 |
| HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm | 215 | ℃ | ISO 75/Be |
| HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm | 190 | ℃ | ISO 75/Ae |
| HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm | 215 | ℃ | ISO 75/Bf |
| HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm | 190 | ℃ | ISO 75/Af |
| Relative Temp Index,Elec | 75 | ℃ | UL 746B |
| Relative Temp Index,Mech w/impact | 75 | ℃ | UL 746B |
| Relative Temp Index,Mech w/o impact | 75 | ℃ | UL 746B |
| PHYSICAL | Value | Unit | Standard |
| Specific Gravity | 1.5 | - | ASTM D 792 |
| Filler Content | 10 | % | ASTM D 229 |
| Mold Shrinkage on Tensile Bar,flow(2)(5) | 0.6-1 | % | SABIC Method |
| Mold Shrinkage on Tensile Bar,xflow(2)(5) | 0.7-1.2 | % | SABIC Method |
| Melt Flow Rate,266℃/5.0 kgf | 110 | g/10 min | ASTM D 1238 |
| Density | 1.5 | g/cm³ | ISO 1183 |
| Water Absorption,(23℃/sat) | 0.27 | % | ISO 62 |
| Moisture Absorption(23℃/50% RH) | 0.08 | % | ISO 62 |
| Melt Volume Rate,MVR at 250℃/2.16 kg | 17 | cm³/10 min | ISO 1133 |
| Melt Volume Rate,MVR at 250℃/5.0 kg | 55 | cm³/10 min | ISO 1133 |
| Melt Volume Rate,MVR at 265℃/5.0 kg | 90 | cm³/10 min | ISO 1133 |
| Melt Viscosity,260℃,1500 sec-1 | 90 | Pa-s | ISO 11443 |
| ELECTRICAL | Value | Unit | Standard |
| Volume Resistivity | 1.E+15 | Ohm-cm | ASTM D 257 |
| Hot Wire Ignition{PLC) | 2 | PLC Code | UL 746A |
| Comparative Tracking Index(UL){PLC} | 3 | PLC Code | UL 746A |
| Volume Resistivity | 1.E+15 | Ohm-cm | IEC 60093 |
| Surface Resistivity,ROA | >1.E+15 | Ohm | IEC 60093 |
| FLAME CHARACTERISTICS | Value | Unit | Standard |
| UL Compliant,94V-0 Flame Class Rating(3)(4) | 1 | mm | UL 94 by SABIC-IP |
| Glow Wire Flammability Index 960℃,passes at | 3 | mm | IEC 60695-2-12 |
| Injection Molding | Value | Unit | |
| Drying Temperature | 110-120 | ℃ | |
| Drying Time | 2-4 | hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250-270 | ℃ | |
| Nozzle Temperature | 240-260 | ℃ | |
| Front-Zone 3 Temperature | 245-265 | ℃ | |
| Middle-Zone 2 Temperature | 240-255 | ℃ | |
| Rear-Zone 1 Temperature | 230-245 | ℃ | |
| Hopper Temperature | 40-60 | ℃ | |
| Mold Temperature | 40-100 | ℃ | |
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.