LNP™ STAT-KON™ PC DX13320C compound
聚碳酸酯
碳纤维增强材料
SABIC Innovative Plastics Asia Pacific
产品说明
LNP* Statkon DX13320C is ultra clean polycarbonate/carbon fiber compound with high modulus, good flow ability, easy mold release, and high level of cleanliness for the most demanding application. A unique feature of this material is its low C18-C40 hydrocarbons. This compound is manufactured using LNP CCS Technology.
填料增强:含碳纤维增强
性能特点:Low (to None) Ion Content,流动性良好,易脱模
塑料牌号:PC DX13320C compound
加工方法:注射成型
定属记号:PC
销售电话:185 5121 3137 谭经理
湘樟版权:http://www.xzslw.com/sujiao/pc/stat-kon/dx13320c-compound.html
材料物性
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.27 | g/cm³ | ASTM D792 |
熔流率(300℃/2.16 kg) | 21 | g/10 min | ASTM D1238 |
溶化体积流率(MVR)(300℃/2.16 kg) | 19.0 | cm³/10min | ISO 1133 |
收缩率 | ASTM D955 | ||
流动:24小时 | 0.050 到 0.15 | % | |
横向流动:24小时 | 0.10 到 0.30 | % | |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量2 | 12900 | MPa | ASTM D638 |
抗张强度3(断裂) | 148 | MPa | ASTM D638 |
伸长率3(断裂) | 2.5 | % | ASTM D638 |
弯曲模量4(50.0 mm 跨距) | 11700 | MPa | ASTM D790 |
弯曲强度4(断裂,50.0 mm 跨距) | 231 | MPa | ASTM D790 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
悬壁梁缺口冲击强度(23℃) | 93 | J/m | ASTM D256 |
无缺口悬臂梁冲击(23℃) | 500 | J/m | ASTM D4812 |
注射 | 额定值 | 单位制 | |
干燥温度 | 90.0 到 100 | ℃ | |
干燥时间 | 3.0 到 5.0 | hr | |
螺筒后部温度 | 265 到 280 | ℃ | |
螺筒中部温度 | 270 到 310 | ℃ | |
螺筒前部温度 | 275 到 310 | ℃ | |
射嘴温度 | 280 到 310 | ℃ | |
加工(熔体)温度 | 280 到 310 | ℃ | |
模具温度 | 70.0 到 110 | ℃ | |
背压 | 0.300 到 1.00 | MPa | |
螺杆转速 | 20 到 100 | rpm |