Petra® PET 330 FR BK-112
30%玻璃纤维增强材料
PET
聚对苯二甲酸乙二醇酯
BASF Corporation
产品说明:
Petra 330 FR BK-112 is a 30% glass reinforced, flame retardant PET, pigmented black injection molding compound rated UL94 V-0 in a 1/64 inch thickness. The product is designed for injection molding of thin and complex parts such as electrical bobbins. Due to its high crystallization rate the processability of the product in the injection molding process is very good. It exhibits excellent balance of properties including strength, stiffness, HDT, dimensional resistance and electrical properties.
Applications
Electrical/electronic application including connectors, bobbins, sockets, ciol, switches, relays, covers and housings.
黄卡下载：E36632-231236
填料增强：含30%玻璃纤维增强材料
材料特性：尺寸稳定性良好，刚性良好，可加工性良好，良好的电气性能，良好的强度，阻燃性
材料用途：保护性遮盖物，电气/电子应用领域，开关，连接器，外壳，线轴
加工方法：注射成型
产品颜色：黑色粒子
杜邦销售：苏州希普能工程塑料 185 5121 3137 谭经理
塑料牌号：PET 330 FR BK-112
版权所有：http://www.xzslw.com/sujiao/pet/petra/330-fr-bk-112.html
产品物性：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 比重 | 1.67 | g/cm³ | ASTM D792 |
| 收缩率 - 流动(3.18 mm) | 0.30 | % | |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度(R 级) | 118 | ASTM D785 | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 抗张强度 | ASTM D638 | ||
| 断裂,-40℃ | 170 | MPa | |
| 断裂,23℃ | 135 | MPa | |
| 断裂,80℃ | 82.0 | MPa | |
| 断裂,121℃ | 60.0 | MPa | |
| 伸长率 | ASTM D638 | ||
| 断裂,-40℃ | 2.0 | % | |
| 断裂,23℃ | 2.0 | % | |
| 断裂,80℃ | 4.1 | % | |
| 断裂,121℃ | 5.7 | % | |
| 弯曲模量(23℃) | 9930 | MPa | ASTM D790 |
| 弯曲强度(23℃) | 215 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 悬壁梁缺口冲击强度(23℃) | 90 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度(1.8 MPa,未退火) | 223 | ℃ | ASTM D648 |
| 熔融峰值温度 | 250 | ℃ | ASTM D3418 |
| RTI Elec | UL 746 | ||
| 0.300 mm | 75.0 | ℃ | |
| 0.750 mm | 155 | ℃ | |
| 1.50 mm | 155 | ℃ | |
| 3.00 mm | 155 | ℃ | |
| RTI Imp | UL 746 | ||
| 0.300 mm | 75.0 | ℃ | |
| 0.750 mm | 155 | ℃ | |
| 1.50 mm | 155 | ℃ | |
| 3.00 mm | 155 | ℃ | |
| RTI | UL 746 | ||
| 0.300 mm | 75.0 | ℃ | |
| 0.750 mm | 155 | ℃ | |
| 1.50 mm | 155 | ℃ | |
| 3.00 mm | 155 | ℃ | |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 体积电阻率(1.50 mm) | > 1.0E+13 | ohm·cm | ASTM D257 |
| 介电强度3(1.50 mm) | 29 | kV/mm | ASTM D149 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 0.300 mm | V-0 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 120 | ℃ | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 加工（熔体）温度 | 280 到 300 | ℃ | |
| 模具温度 | 100 到 110 | ℃ | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||
| 备注 3 方法A（短时间） |
|||
苏州希普能塑料代理销售原产原包杜邦PET材料，由于价格时常浮动网上就不一一报价，还请电话咨询价格，谢谢关照！