LNP STAT-LOY PMMA 93000LTH

添加时间：2013-02-22 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料

LNP™ STAT-LOY™ Compound PMMA 93000LTH

Also known as:LNP™ Stat-loy™ Compound 93000LTH Product reorder name:93000LTH

LNP* Stat-Loy* 93000LTH is a compound based on Acrylic resin featuring a permanent anti-static characteristic. Added features include: Transparent and Formulation Locked.

Property

TYPICAL PROPERTIES(1)

MECHANICAL	Value	Unit	Standard
Tensile Stress,brk,Type I,5mm/min	400	kgf/cm²	ASTM D 638
Tensile Strain,brk,Type I,5mm/min	7	%	ASTM D 638
Tensile Modulus,5mm/min	18200	kgf/cm²	ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span	470	kgf/cm²	ASTM D 790
Flexural Modulus,1.3mm/min,50mm span	14900	kgf/cm²	ASTM D 790
IMPACT	Value	Unit	Standard
Izod Impact,unnotched,23℃	68	cm-kgf/cm	ASTM D 4812
Izod Impact,notched,23℃	4	cm-kgf/cm	ASTM D 256
THERMAL	Value	Unit	Standard
HDT,1.82 MPa,3.2mm,unannealed	66	℃	ASTM D 648
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.15	-	ASTM D 792
ELECTRICAL	Value	Unit	Standard
Volume Resistivity	1.E+09-1.E+11	Ohm-cm	ASTM D 257
Surface Resistivity	1.E+09-1.E+11	Ohm	ASTM D 257
Static Decay,5000V to <50V	<1	< seconds	FTMS101B
Source GMD,last updated:2011/06/27

Parameter Injection Molding	Value	Unit
Drying Temperature	70-80	℃
Drying Time	4	hrs
Maximum Moisture Content	0.05-0.1	%
Melt Temperature	200-210	℃
Front-Zone 3 Temperature	205-215	℃
Middle-Zone 2 Temperature	195-205	℃
Rear-Zone 1 Temperature	180-195	℃
Mold Temperature	10-50	℃
Back Pressure	0.2-0.3	MPa
Screw Speed	30-60	rpm
Source GMD, last updated:2011/06/27