PMMA 7H 流动性良好,耐气候影响,高强度

添加时间：2013-10-19 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料

Plexiglas PMMA 7H

Plexiglas® PMMA 7H

聚甲基丙烯酸甲酯-丙烯酸

Evonik Industries AG

产品说明

Product Profile:

PLEXIGLAS® 7H is an amorphous thermoplastic molding compound (PMMA).

Typical properties of PLEXIGLAS® molding compounds are:

﹒good flow

﹒high mechanical strength, surface hardness and mar resistance

﹒high light transmission

﹒excellent weather resistance

﹒free colorability due to crystal clarity.

Special properties of PLEXIGLAS® 7H are:

﹒very good mechanical properties

﹒high heat deflection temperature

﹒high melt strength

﹒AMECA listing.

Application:

Used for extruding optical and technical profiles and sheets.

Examples:

sheets, tubes, multi-skin sheets, coextrusion of window profiles and similar applications

Processing:

PLEXIGLAS® 7H can be processed on extruders with 3-zone general purpose screws for engineering thermoplastics.

Physical Form / Packaging:

PLEXIGLAS® molding compounds are supplied as pellets of uniform size, packaged in 25kg polyethylene bags or in 500kg boxes with PE lining; other packaging on request.

UL黄卡²：E65495-247805

材料特点：High Hardness，高强度，着色好，流动性良好，耐气候影响

材料用途：管道，门窗，片材，型材

加工方法：共挤出成型，挤出

定属记号：丙烯酸 (PMMA)

塑料牌号：PMMA 7H

销售电话：185 5121 3137 谭经理

材料物性

物理性能	额定值	单位制	测试方法
密度	1.19	g/cm³	ISO 1183
溶化体积流率(MVR)(230℃/3.8kg)	1.40	cm³/10min	ISO 1133
机械性能	额定值	单位制	测试方法
拉伸模量	3200	MPa	ISO 527-2/1
拉伸应力(断裂)	76.0	MPa	ISO 527-2/5
拉伸应变(断裂)	5.5	%	ISO 527-2/5
冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度(23℃)	20	kJ/m²	ISO 179/1eU
热性能	额定值	单位制	测试方法
热变形温度
0.45 MPa,未退火	100	℃	ISO 75-2/B
1.8 MPa,未退火	95.0	℃	ISO 75-2/A
玻璃转化温度	112	℃	IEC 1006
维卡软化温度	103	℃	ISO 306/B50
线形膨胀系数-流动(0 到 50℃)	0.000080	cm/cm/℃	ISO 11359-2
可燃性	额定值		测试方法
UL 阻燃等级(1.60 mm)	HB		UL 94
光学性能	额定值	单位制	测试方法
折射率	1.49		ISO 489
透射率³	92.0	%	ISO 13468-2
雾度	<0.50	%	ASTM D1003
补充信息	额定值		测试方法
Fire Rating	B2		DIN 4102
挤出	额定值		单位制
干燥温度	<93.0		℃
干燥时间	2.0 到 3.0		hr
熔体温度	220 到 260		℃
模具温度	220 到 260		℃