PMMA df23 7H 高强度,流动性佳,耐气候影响
添加时间:2013-11-27 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
Plexiglas® PMMA df23 7H
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
产品说明
Product Profile:
PLEXIGLAS® Satinice df23 7H, based on PLEXIGLAS® 7H, is characterized by diffuse scattering of light.
Typical properties of PLEXIGLAS® molding compound are
﹒good flow
﹒high mechanical strength, surface hardness and mar resistance
﹒very good weather resistance.
Special properties of PLEXIGLAS® Satinice df23 7H are
﹒excellent lightdiffusion combined with excellent light transmission,
﹒matte surfaces can be obtained by varying the extrusion parameters.
Application:
Used for extruding profiles and sheets for lighting engineering applications
Examples:
luminaire covers, displays, projection screens and similar applications
Processing:
PLEXIGLAS® Satinice df23 7H can be processed on extruders with 3-zone general purpose screws for engineering thermoplastics. The matte finish of profile surfaces depends very much on machine design (calibrating unit, polishing rolls) and cooling conditions. It can be enhanced by controlled temperature reduction.
Physical Form / Packaging:
PLEXIGLAS® Satinice df molding compounds are supplied as pellets of uniform size, packaged in 25kg polyethylene bags; other packaging on request.
UL 黄卡2:E65495-100986375
材料特点:High Hardness,Light Stabilized,高强度,流动性佳,耐气候影响
材料用途:Displays,片材,型材,照明漫射器
产品形式:颗粒料
加工方法:挤出
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA df23 7H
销售电话:185 5121 3137 谭经理
材料物性
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.19 | g/cm³ | ISO 1183 |
溶化体积流率(MVR)230℃/3.8 kg) | 0.950 | cm³/10min | ISO 1133 |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 3400 | MPa | ISO 527-2/1 |
拉伸应力(断裂) | 70.0 | MPa | ISO 527-2/5 |
拉伸应变(断裂) | 6.0 | % | ISO 527-2/5 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度(23℃) | 1.8 | kJ/m² | ISO 179/1 |
简支梁缺口冲击强度(23℃) | 20 | kJ/m² | ISO 179/1eU |
热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 | |||
0.45 MPa,未退火 | 101 | ℃ | ISO 75-2/B |
1.8 MPa,未退火 | 97.0 | ℃ | ISO 75-2/A |
玻璃转化温度 | 106 | ℃ | IEC 1006 |
维卡软化温度 | 105 | ℃ | ISO 306/B50 |
线形膨胀系数-流动(0 到 50℃) | 0.000063 | cm/cm/℃ | ISO 11359-2 |
可燃性 | 额定值 | 单位制 | 测试方法 |
热灯丝点火温度 | 700 | ℃ | IEC 60695-2-13 |
光学性能 | 额定值 | 单位制 | 测试方法 |
透射率3 | 81.0 | % | ISO 13468-2 |
补充信息 | 额定值 | 单位制 | 测试方法 |
Fire Rating | B2 | DIN 4102 | |
Half-Value Angle | 21 | ° | DIN 5036 |
挤出 | 额定值 | 单位制 | |
干燥温度 | <95.0 | ℃ | |
干燥时间 | 2.0 到 3.0 | hr | |
熔体温度 | 220 到 260 | ℃ | |
模具温度 | 220 到 260 | ℃ |