Plexiglas® PMMA Hi-Gloss NTA-3
聚甲基丙烯酸甲酯-丙烯酸
Evonik Industries AG
产品说明
Product Profile:
PLEXIGLAS® Hi-Gloss NTA-3 is a compound with an increased heat deflection temperature based on polymethyl methacrylate (PMMA).
Besides the well-known properties of PLEXIGLAS® molding compound, such as
﹒good flow
﹒high mar resistance
﹒good weather resistance
﹒good polishability,
PLEXIGLAS® Hi-Gloss NTA-3 offers the added benefit of
﹒increased heat deflection temperature under load.
Application:
PLEXIGLAS® Hi-Gloss NTA-3 is particularly suitable for injection molding technical components.
Owing to its superior brilliance, high-gloss (Class A) surfaces can be obtained in opaque colors.
Examples:
automotive body parts: window channels, pillar panels
材料特点:高光泽,高抗撞击,流动性高,耐气候影响
材料用途:Automotive Backlights,Automotive Window Encapsulation,汽车防撞杆,汽车领域的应用,汽车外部零件,汽车外部装饰
产品外观:不透明
产品形式:颗粒料
加工方法:注射成型
定属记号:丙烯酸 (PMMA)
塑料牌号:PMMA Hi-Gloss NTA-3
销售电话:185 5121 3137 谭经理
材料物性
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.18 | g/cm³ | ISO 1183 |
溶化体积流率(MVR)(230℃/3.8 kg) | 2.00 | cm³/10min | ISO 1133 |
吸水率(23℃,24 hr) | >3.0 | % | ISO 62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 2900 | MPa | ISO 527-2/1 |
拉伸应力(断裂) | 60.0 | MPa | ISO 527-2/5 |
拉伸应变(断裂) | 2.6 | % | ISO 527-2/5 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度(23℃) | 16 | kJ/m² | ISO 179/1eU |
热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 | |||
0.45 MPa,未退火 | 106 | ℃ | ISO 75-2/B |
1.8 MPa,未退火 | 106 | ℃ | ISO 75-2/A |
玻璃转化温度 | 126 | ℃ | ISO 11357-2 |
维卡软化温度 | 116 | ℃ | ISO 306/B50 |
可燃性 | 额定值 | 单位制 | 测试方法 |
热灯丝点火温度 | 675 | ℃ | IEC 60695-2-13 |
补充信息 | 额定值 | 测试方法 | |
Fire Rating | B2 | DIN 4102 | |
注射 | 额定值 | 单位制 | |
干燥温度 | <100 | ℃ | |
干燥时间 | 2.0 到 3.0 | hr | |
加工(熔体)温度 | 220 到 250 | ℃ | |
模具温度 | 50.0 到 85.0 | ℃ |