PMMA Resist zk4HC 高抗冲击,耐气候,高清晰度

添加时间：2013-11-29 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料

Plexiglas PMMA Resist zk4HC

Plexiglas® PMMA Resist zk4HC

聚甲基丙烯酸甲酯-丙烯酸

Evonik Industries AG

产品说明

Product Profile:

PLEXIGLAS® Resist zk4HC is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified PLEXIGLAS® molding compounds are

﹒high weather resistance

﹒excellent transmission and clarity

﹒brilliant appearance

﹒the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk4HC is characterized by the

following special properties:

﹒improved break resistance and impact strength

﹒best resistance to stress cracking of all impact-modified PLEXIGLAS molding compounds

﹒AMECA listing.

Application:

Used for extruding and coextruding sheets and profiles.

Examples:

extruded/coextruded sheets and profiles for automotive bodies and the sanitaryware sector (bathtubs and shower trays) or crystal-clear luminare covers for industrial plants that come into contact with aggressive media.

UL 黄卡²：E65495-247817

含添加剂：冲击调节器

材料特点：高 ESCR（抗应力裂纹），高抗撞击，耐气候影响，高清晰度，外观良好

材料用途：保护性遮盖物，片材，汽车防撞杆，汽车领域的应用，汽车外部零件，汽车外部装饰，卫浴产品，型材

产品形式：颗粒料

加工方法：共挤出成型，挤出

定属记号：丙烯酸 (PMMA)

塑料牌号：PMMA Resist zk4HC

销售电话：185 5121 3137 谭经理

材料物性

物理性能	额定值	单位制	测试方法
密度	1.18	g/cm³	ISO 1183
溶化体积流率(MVR)(230℃/3.8 kg)	1.10	cm³/10min	ISO 1133
吸水率			ISO 62
23℃,24 hr	2.0	%
平衡,23℃,50% RH	0.60	%
机械性能	额定值	单位制	测试方法
拉伸模量	2900	MPa	ISO 527-2/1
拉伸应力(屈服)	68.0	MPa	ISO 527-2/50
拉伸应变(屈服)	4.5	%	ISO 527-2/50
断张率	17	%	ISO 527-2
冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度(23℃)	25	kJ/m²	ISO 179/1eU
热性能	额定值	单位制	测试方法
玻璃转化温度	108	℃	ISO 11357-2
维卡软化温度	102	℃	ISO 306/B50
线形膨胀系数-流动(0 到 50℃)	0.000080	cm/cm/℃	ISO 11359-2
可燃性	额定值		测试方法
UL 阻燃等级(1.60 mm)	HB		UL 94
光学性能	额定值	单位制	测试方法
折射率	1.490		ISO 489
透射率³	92.0	%	ISO 13468-2
补充信息	额定值		测试方法
Fire Rating	B2		DIN 4102
挤出	额定值		单位制
干燥温度	<90.0		℃
干燥时间	2.0 到 3.0		hr
熔体温度	220 到 260		℃
模具温度	220 到 260		℃