PPS 1342L4 玻纤40增强,含PTFE润滑剂
添加时间:2013-05-21 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
FORTRON® 1342L4 SD3002 BLACK
FORTRON® 1342L4 SD3002 BLACK H
FORTRON® 1342L4 SF3001 NATURAL
FORTRON® 1342L4 SG3005 BLUE
FORTRON 1342L4 | PPS | Specialty
Description
Fortron 1342L4 is a low wear grade, ideally suited for bearings, gears and other sliding friction/wear applications. This product is glass fiber reinforced and contains PTFE.
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.
Melt temperature 320-340 degC
Mold wall temperature at least 140 degC
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
ISO Data | Physical properties | Value | Unit | Test Standard |
Phys | Density | 1690 | kg/m³ | ISO 1183 |
Mold shrinkage - parallel | 0.2 | % | ISO 294-4 | |
Mold shrinkage - normal | 0.5 | % | ISO 294-4 | |
Water absorption (23℃-sat) | 0.02 | % | ISO 62 | |
Mech | Mechanical properties | Value | Unit | Test Standard |
Tensile modulus (1mm/min) | 14400 | MPa | ISO 527-2/1A | |
Tensile stress at break (5mm/min) | 165 | MPa | ISO 527-2/1A | |
Tensile strain at break (5mm/min) | 1.6 | % | ISO 527-2/1A | |
Flexural modulus (23℃) | 13700 | MPa | ISO 178 | |
Flexural stress @ break | 245 | MPa | ISO 178 | |
Charpy impact strength @ 23℃ | 44 | kJ/m² | ISO 179/1eU | |
Charpy notched impact strength @ 23℃ | 8.5 | kJ/m² | ISO 179/1eA | |
Charpy notched impact strength @ -30℃ | 8.5 | kJ/m² | ISO 179/1eA | |
Notched impact strength (Izod) @ 23℃ | 8.5 | kJ/m² | ISO 180/1A | |
Notched impact strength (Izod) @-30℃ | 8.5 | kJ/m² | ISO 180/1A | |
Coefficient of friction against steel - static | 0.2 | - | ISO 8295 | |
Therm | Thermal properties | Value | Unit | Test Standard |
Melting temperature (10℃/min) | 280 | ℃ | ISO 11357-1,-2,-3 | |
Glass transition temperature (10℃/min) | 90 | ℃ | ISO 11357-1,-2,-3 | |
DTUL @ 1.8 MPa | 270 | ℃ | ISO 75-1/-2 | |
DTUL @ 8.0 MPa | 215 | ℃ | ISO 75-1/-2 | |
Coeff.of linear therm. expansion (parallel) | 0.22 | E-4/℃ | ISO 11359-2 | |
Coeff.of linear therm. expansion (normal) | 0.4 | E-4/℃ | ISO 11359-2 | |
Flammability @1.6mm nom. thickn. | V-0 | class | UL94 | |
thickness tested (1.6) | 1.5 | mm | UL94 | |
Flammability at thickness h | V-0 | class | UL94 | |
thickness tested (h) | 0.75 | mm | UL94 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3 - 4
Drying temperature (℃):130 - 140