PVDF 31508/0003 颗粒料,挤出级
添加时间:2013-10-04 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
3M™ Dyneon™ Fluoroplastic PVDF 31508/0003
聚偏二氟乙烯
3M Advanced Materials Division
产品说明:
3M™ Dyneon™ PVDF 31508/0003 is a flexible copolymer of VF2 and CTFE, exhibiting very low shrinkage and excellent impact resistance. PVDF 31508/0003 also has a very low brittleness temperature, for excellent low temperature performance. This material is ideal for insulation and buffering materials for wire and cable applications and for tubing. PVDF 31508/0003 has excellent flame and smoke performance, with an LOI of 65. PVDF 31508/0003 is designed for high speed extrusion, and can be processed using a variety of conventional thermoplastic conversion techniques. As with all PVDF grades, PVDF 31508/0003 also possesses very good chemical and temperature resistance.
Features and Benefits
•Copolymer of VF 2 and CTFE
•Ultra-flexible
•Very low shrinkage rates
•Wide operating temperature window
•Processable using a variety of thermoplastic conversion techniques
•Excellent low flame and low smoke performance
材料特点:共聚物,高抗撞击,良好的柔韧性,耐低温,耐化学,高耐热,收缩性低,低烟释放,阻燃
材料用途:电线电缆应用,管道,绝缘材料
产品形式:颗粒料
加工方法:挤出
Category:Polymers -- Thermoplastics -- Fluoroplastics
3 M 代理:苏州希普能工程塑料 185 5121 3137 谭经理
物料数据
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.76 | g/cm³ | ISO 1183 |
熔流率(熔体流动速率) | ASTM D1238 | ||
230℃/2.16 kg | 5.0 | g/10 min | |
230℃/5.0 kg | 15 | g/10 min | |
吸水率(24 hr,23℃) | < 0.040 | % | ISO 62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
抗张强度1(断裂,23℃) | 22.0 | MPa | ASTM D638 |
伸长率1(断裂,23℃) | 480 | % | ASTM D638 |
弯曲模量2(23℃) | 425 | MPa | ASTM D790 |
热性能 | 额定值 | 单位制 | 测试方法 |
脆化温度 | -37.0 | ℃ | ASTM D746A |
熔融峰值温度 | 169 | ℃ | ASTM D3418 |
电气性能 | 额定值 | 单位制 | 测试方法 |
表面电阻率3 | > 1.0E+14 | ohms | ASTM D257 |
体积电阻率4(23℃) | > 1.0E+14 | ohms·cm | ASTM D257 |
介电常数(1 MHz) | 7.00 | ASTM D150 | |
可燃性 | 额定值 | 单位制 | 测试方法 |
UL 阻燃等级 | V-0 | UL 94 | |
极限氧指数(3.00 mm) | 65 | % | ASTM D2863 |
备注 1 50 mm/min 2 2.0 mm/min 3 Voltage <1V,after 2 Minutes - 500V 4 Intensity = 10 mA,after 2 Minutes |