Kynar Flex® 2850-00
聚偏二氟乙烯
Arkema Technical Polymers
产品说明:
Kynar Flex® resins are fluorinated thermoplastic copolymers.
Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties.
Main applications: piping systems, corrosion protection in the chemical industry and lined pipe, off shore, wire and cable.
Kynar Flex® 2850-00 resin is a standard grade of granules less flexible than the grade Kynar Flex® 2800-00 resin with a higher melting point. For extrusion, wire and cable constructions which require an UL wire ratings to 150 degrees C.
Also for applications requiring a UL RTI temperature rating of 140 degrees C.
A powder form is available as Kynar Flex® 2851-00 resin.
黄卡下载:E54699-244852
含添加剂:热稳定剂、紫外线稳定剂
材料特点:UV Stabilized、纯度高、共聚物、抗紫外线性能良好、耐化学性良好、热稳定性、阻隔树脂
材料应用:电线电缆应用、管道系统
外观形式:颗粒
供货地区:北美洲、非洲和中东、拉丁美洲、欧洲、亚太地区
加工方法:挤出、树脂传递成型、型材挤出成型
中国代理:苏州希普能工程塑料 185 5121 3137 谭经理
物料数据
物理性能 | 额定值 | 单位制 | 测试方法 |
密度 | 1.77 | g/cm³ | ISO 1183 |
熔融体积流量(MVR)(230℃/5.0 kg) | 1.10 | cm³/10min | ISO 1133 |
吸水率 | ISO 62 | ||
饱和,23℃ | 0.030 | % | |
平衡,23℃,50% RH | 0.015 | % | |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 1300 | MPa | ISO 527-2 |
拉伸应力(屈服) | 40.0 | MPa | ISO 527-2 |
拉伸应变(屈服) | 11 | % | ISO 527-2 |
标称拉伸断裂应变 | > 50 | % | ISO 527-2 |
拉伸蠕变模量 | ISO 899-1 | ||
1 hr | 508 | MPa | |
1000 hr | 210 | MPa | |
冲击性能 | 额定值 | 单位制 | 测试方法 |
简支梁缺口冲击强度 | ISO 179/1eA | ||
-30℃ | 5.0 | kJ/m² | |
23℃ | 无断裂 | ||
热性能 | 额定值 | 单位制 | 测试方法 |
热变形温度 | |||
0.45 MPa,未退火 | 114 | ℃ | ISO 75-2/B |
1.8 MPa,未退火 | 46.0 | ℃ | ISO 75-2/A |
玻璃转化温度1 | -43.0 | ℃ | ISO 11357-2 |
维卡软化温度 | 107 | ℃ | ISO 306/B50 |
熔融温度1 | 158 | ℃ | ISO 11357-3 |
线形热膨胀系数 - 流动 | 1.6E-4 | cm/cm/℃ | ISO 11359-2 |
电气性能 | 额定值 | 单位制 | 测试方法 |
表面电阻率 | 1.0E+13 | ohms | IEC 60093 |
体积电阻率 | 2.0E+14 | ohms·cm | IEC 60093 |
介电强度 | 21 | kV/mm | IEC 60243-1 |
相对电容率 | IEC 60250 | ||
100 Hz | 10.5 | ||
1 MHz | 6.50 | ||
耗散因数 | IEC 60250 | ||
100 Hz | 0.038 | ||
1 MHz | 0.23 | ||
漏电起痕指数 | 600 | V | IEC 60112 |
可燃性 | 额定值 | 单位制 | 测试方法 |
可燃性等级(1.5 mm) | V-0 | IEC 60695-11-10,-20 | |
V-0 | |||
极限氧指数 | 43 | % | ISO 4589-2 |
备注 1 10℃/min |