添加时间：2018-10-03 信息来源：http://www.xzslw.com/ 作者：苏州希普能塑料
Kynar Flex® 2950-05
聚偏二氟乙烯
Arkema Technical Polymers
产品说明:
Kynar Flex® resins are fluorinated thermoplastic copolymers.
Kynar Flex® 2950-05 resin is a pelletized, semi-crystalline VF2 based copolymer. It has been designed for wire and cable applications requiring high flexibility and improved resistance to impact.The low molecular weight allows extrusion conditions that reduce jacket shrink back over fiber optic constructions.
Additional characteristics:
●Excellent thermal stability
●Excellent abrasion resistance
●Excellent chemical resistance
●Impervious to UV degradation
●High Limiting Oxygen Index
●Extremely low smoke emission characteristics
Meets UL910 requirements
材料特点：High Flexibility、半结晶、低分子量、低烟度、共聚物、抗紫外线性能良好、良好抗撞击性、良好耐磨损性、耐化学、热稳定
材料应用：电线电缆应用
外观形式：粒子
供货地区：北美洲、非洲和中东、拉丁美洲、欧洲、亚太地区
加工方法：挤出
中国代理：苏州希普能工程塑料 185 5121 3137 谭经理
物料数据
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.77 | g/cm³ | ISO 1183 |
| 熔融体积流量（MVR）(232℃/3.8 kg) | 11.5 | cm³/10min | ISO 1133 |
| 吸水率(饱和,23℃) | 0.030 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | 387 | MPa | ISO 527-2 |
| 拉伸应力(屈服) | 17.0 | MPa | ISO 527-2 |
| 拉伸应变(屈服) | 18 | % | ISO 527-2 |
| 标称拉伸断裂应变 | > 50 | % | ISO 527-2 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度(23℃) | 无断裂 | ISO 179/1eA | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 热变形温度 | |||
| 0.45 MPa,未退火 | 57.0 | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 43.0 | ℃ | ISO 75-2/A |
| 玻璃转化温度1 | -34.0 | ℃ | ISO 11357-2 |
| 熔融温度1 | 134 | ℃ | ISO 11357-3 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 体积电阻率 | 2.0E+14 | ohms·cm | IEC 60093 |
| 介电强度 | 1.4 | kV/mm | IEC 60243-1 |
| 相对电容率(100 Hz) | 7.05 | IEC 60250 | |
| 耗散因数(100 Hz) | 0.12 | IEC 60250 | |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| 可燃性等级(1.5 mm) | V-0 | IEC 60695-11-10,-20 | |
| V-0 | |||
| 极限氧指数 | 95 | % | ISO 4589-2 |
| 备注 1 10℃/min |
|||