Kynar Flex® ADX 2250-05E

聚偏二氟乙烯

Arkema Technical Polymers

产品说明:

Kynar Flex® resins are fluorinated thermoplastic copolymers.

Kynar Flex® ADX 2250-05 resin is a semi-crystalline flexible functionalized copolymer designed for co-extrusion with other materials to improve interlayer adhesion. It is particularly suited to tubing, pipe and film co-extrusion applications.

Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties.

More over, this grade increases the potential of adhesion on materials as polyamides, polyolefins and can be coextruded.

含添加剂：紫外线稳定剂

材料特点：UV Stabilized、半结晶、纯度高、共聚物、抗紫外线性能良好、耐化学、阻隔树脂

材料用途：薄膜、管道系统、管件

供货地区：北美洲、非洲和中东、拉丁美洲、欧洲、亚太地区

外观形式：粒子

加工方法：薄膜挤出、吹塑成型、共挤薄膜、共挤出成型、挤出、片材挤出成型、树脂传递成型

中国代理：苏州希普能工程塑料 185 5121 3137 谭经理

物料数据

物理性能	额定值	单位制	测试方法
密度	1.79	g/cm³	ISO 1183
熔融体积流量（MVR）(230℃/3.8 kg)	6.00	cm³/10min	ISO 1133
吸水率(饱和,23℃)	0.10	%	ISO 62
机械性能	额定值	单位制	测试方法
拉伸应力(屈服)	12.0	MPa	ISO 527-2
拉伸应变(屈服)	18	%	ISO 527-2
标称拉伸断裂应变	> 50	%	ISO 527-2
热性能	额定值	单位制	测试方法
热变形温度(1.8 MPa,未退火)	33.0	℃	ISO 75-2/A
熔融温度¹	123	℃	ISO 11357-3
电气性能	额定值	单位制	测试方法
介电强度	13	kV/mm	IEC 60243-1
备注 ¹ 10℃/min