DuPontT Teflon® FEP 6100 Fluoropolymer Resin
Technical DataSheet
DuPontT Teflon® FEP 6100 fluoropolymer resin is a melt-processable fluoropolymer resin specifically designed for high-speed extrusion of thin coatings on small-gauge wires for twisted-pair constructions.As shown in Table 1, this resin provides the electrical and mechanical properties needed for low voltage applications. In addition, Teflon® FEP 6100 has a higher melt flow rate than most other fluoropolymer resins. This permits higher extrusion speeds and easier processing, making Teflon® FEP 6100 a cost-effective alternative for producing thin-wall extrusions.Teflon® FEP 6100 possesses a balance of processing and performance properties, which makes it an excellent choice for many applications. Like all Teflon® fluoropolymer resins, Teflon® FEP 6100 offers an excellent combination of properties:low flammabilityexceptional dielectric propertiesheat resistancetoughnessflexibilitylow coefficient of frictionnonstick characteristicsnegligible moisture absorptionchemical inertnessperformance at temperature extremesweather resistanceApplicationsTeflon® FEP 6100 is especially suitable for use in insulating data and telecommunications cables with excellent fire performance and physical properties as well as outstanding electrical performance. Cables insulated with Teflon® FEP 6100 have met the requirements of the NFPA 90A 'Standard for the Installation of Air-conditioning and Ventilating Systems'. To meet these requirements cables are tested using the NFPA 262 Standard Method of Test for Flame Travel and Smoke of Wires and Cables. This standard test method is used to qualify cables for installation in plenum spaces under the provisions of NFPA 90A. Teflon® FEP 6100 complies with ASTM 2116.Teflon® FEP 6100 is not recommended as a jacket material or as a heavy-walled insulation in constructions where significant thermal cycling may raisestress-cracking concerns.
DuPontT Teflon® FEP 6100 Fluoropolymer Resin Product details
产品类型:含氟聚合物>聚全氟乙丙烯FEP
产品状态:有售
代理销售:苏州希料能塑料 185 5121 3137 谭经理
DuPontT Teflon® FEP 6100 Fluoropolymer Resin Properties
物理性质 | 值和单位 | 测试条件 | 测试方法 |
比重 | 2.14 g/cc | ASTM D792 | |
熔体流动 | 30 g/10 min | ASTM D2116 | |
吸水率 | < 0.01 % | 24小时;ASTM D570 | |
电气性能 | 值和单位 | 测试条件 | 测试方法 |
体积电阻率 | >1.000E+018 ohm-cm | ASTM D 257 | |
表面电阻率每平方 | >1.000E+016 ohm | ASTM D 257 | |
绝缘强度 | 53 kV/mm | 100微米的薄膜;ASTM D149 | |
电弧电阻 | >300 sec | ASTM D495 | |
介电常数 | 2.03 | @Frequency 1000000 Hz | ASTM D2520 |
耗散因子 | 0.00057 | @Frequency 1000000 Hz | ASTM D2520 |
加工性能 | 值和单位 | 测试条件 | 测试方法 |
加工温度 | 360-385℃ | 固化温度 | |
热性能 | 值和单位 | 测试条件 | 测试方法 |
可燃性,UL94 | V-0 | ||
氧指数 | >95 % | 极限氧指数;ASTM D2863 | |
熔点 | 264℃ | ASTM D3418 | |
机械性能 | 值和单位 | 测试条件 | 测试方法 |
摩擦系数 | 0.08-0.3 | ASTM D1894 | |
弯曲模量 | 0.52 Gpa | ASTM D790 | |
悬臂梁缺口冲击强度 | 9999 J/m | ASTM D256 | |
邵氏硬度 | 56 | ASTM D2240 | |
极限抗拉强度 | 20 Mpa | ASTM D1457 | |
断裂伸长率 | 3 | ASTM D1457 | |
描述性的属性 | |||
耐气候性 | 20 | 在佛罗里达没有受到影响 | |
硫酸传输, g/100sq in. | 0.00001 | ||
水传输, g/100sq in. | 0.4 | ||
红烟硝酸传输, g/100sq in. | 7.5-1.4 | ||
铝的耐盐性,小时 | >744 | ||
燃烧热 J/g | 5100 | ASTM D240 | |
己烷传输, g/100sq in. | 0.56 | ||
哌啶传输, g/100sq in. | 0.04 | ||
喷砂钢板上的抗洗涤剂,小时 | 480 | ||
乙酸乙酯的传输, g/100sq in. | 0.76 | ||
耐折度, # cycles, .18-.20 mm | 5-80 E3 | ||
耐化学溶剂性 | Excellent | ||
铝的耐洗涤剂性,小时 | 744 | ||
洗涤剂抵抗.喷砂铝,小时 | 600 | ||
苯的传输, g/100sq in. | 0.64 | ||
四氯化碳传输, g/100sq in. | 0.31 | ||
醋酸传输, g/100sq in. | 0.41 | ||
丙酮传输, g/100sq in. | 0.95 | ||
苯乙酮的传输, g/100sq in. | 0.5 | ||
20%盐酸传输, g/100sq in. | <0.02 | ||
50%氢氧化钠传输, g/100sq in. | <.02 |