添加时间:2013-12-28  信息来源:http://www.xzslw.com/  作者:苏州希普能塑料
Starpylen TPE MX05038
Starpylen TPE MX05038
热塑性弹性体
Eurostar Engineering Plastics
 
产品说明
Starpylen MX05038 is a TPEX Injection Molding Resin
 
塑料牌号:TPE MX05038
加工方法:注射成型
定属记号:TPE
销售电话:185 5121 3137 谭经理
湘樟版权:http://www.xzslw.com/sujiao/tpe/starpylen/mx05038.html
 
胶料物性
物理性能 额定值 单位制 测试方法
密度 1.09 g/cm³ ISO 1183
机械性能 额定值 单位制 测试方法
拉伸模量 1400 MPa ISO 527-2/1
拉伸应力(屈服) 16.0 MPa ISO 527-2/5
拉伸应变(屈服) 4.3 % ISO 527-2/5
弯曲模量2 1500 MPa ISO 178
弯曲强度2,3 28.0 MPa ISO 178
冲击性能 额定值 单位制 测试方法
悬壁梁缺口冲击强度4(23℃) 8.0 kJ/m² ISO 180/1A
无缺口伊佐德冲击强度4(23℃) 110 kJ/m² ISO 180/1U
热性能 额定值 单位制 测试方法
热变形温度4      
0.45 MPa,未退火,64.0 mm 跨距 96.0 ISO 75-2/Bf
1.8 MPa,未退火,64.0 mm 跨距 58.0 ISO 75-2/Af
线形膨胀系数     ISO 11359-2
流动:23 到 60℃ 0.00011 cm/cm/℃
横向:23 到 60℃ 0.00014 cm/cm/℃
注射 额定值 单位制
干燥温度 70.0
干燥时间 3.0 hr
螺筒后部温度 195 到 205
螺筒中部温度 215 到 225
螺筒前部温度 240 到 250
加工(熔体)温度 225 到 250
模具温度 30.0 到 50.0
PROCESSING PARAMETERS : see above typical molding conditions.
DRYING : is not essential when material is delivered in sealed bags with moisture content below 0.2 %.
BARRELS, SCREWS, MOULDS : use wear resisting steel or alloy such as bimetallic cylinders, nitrided screws.
USE OF REGRIND : the properties of the component should be checked in order to ascertain the maximum acceptable level of regrind.
SAFETY : please refer to Material Safety Datasheet.
 
 
Eurostar Engineering Plastics 40 Years History
 
1972 Creation of Eurostar
 
Fosses is one of the first independent French manufacturing sites dedicated to glass fiber reinforced polyamide manufacturing. One of the founder’s shareholders is the Owens Corning Company that stayed into the capital for more than 10 years.
 
1983 Buy out of Eurostar by Ferro: the company becomes Ferro-Eurostar
 
While still mainly acting in France, Ferro brings resources that increase Eurostar production capacities and implements a mature industrial organization.
 
Starflam brand name starts having an European expansion.
 
Starflam
 
1995 Buy out of Ferro-Eurostar by LNP: the company becomes LNP-Eurostar
 
LNP is an American Company specialized in compounding that was created in 1948. At that time, it was owned by the Kawasaki Steel Company.
 
Ferro’s decision to sell the business is driven by a new company policy orientation that focuses on the historical company skills in Europe (pigments).
 
LNP is one of the global players in highly valued compounds. The sell of Eurostar is an opportunity that the company takes with no hesitation in order to extend its product range with the addition of polyamide and polypropylene compounds.
 
It also brings to Eurostar an access to a new customer’s portfolio and increases the site capabilities to develop engineering compounds. LNP elevates the site quality standards and implements a culture of quality.
 
LNP
 
2002 Buy out of LNP by GE Plastics
 
Following up its buy out by the Nippon Steel Company, Kawasaki Steel focuses its activity on steel manufacturing.
 
GE Pastics makes a strategic investment to position itself on the engineering plastics market one of the product gap at that time whereas the growth potential is high.
 
LNP becomes part of a conglomerate which global strength is not argued.
 
GE opens to LNP R&D capabilities that lead to designing and launching the Starflam Xgen platform, developed and manufactured at Fosses. GE brings to Eurostar a strong culture of risk management and process control and monitoring at each level of the company processes.
 
GE Plastics
 
2007 Buy out of GE Plastics by SABIC 
This new business unit adds up to SABIC traditional business units. It becomes SABIC Innovative Plastics.
 
Sabic
 
2010 Managers Buy Out, company becomes
Starflam
联系湘樟塑料
相关材料
上一页:TPE AA9C1-1001 硬度90A           下一页:TPE AA8C2-1001 硬度80A