添加时间:2014-01-02 信息来源:http://www.xzslw.com/ 作者:苏州希普能塑料
Elastollan® TPU S90A55N
热塑性聚氨酯弹性体(聚酯)
BASF Corp. Thermoplastic Polyurethanes
产品说明
Elastollan® S90A55N is a polyester-based thermoplastic polyurethane (TPU). It exhibits excellent abrasion resistance and toughness, good heat, oil, fuel, and solvent resistance. As with all TPU products, Elastollan® S90A55N must be dried before processing. The drying step is required to maintain a low moisture content until the product enters the processing equipment. The water content must be less than 0.03% before and during processing. The typical drying conditions should be 2-4 hours @ 175°-195℉ (80°-90℃). Elastollan® S90A55N can be stored for up to 1 year in its original container. Containers should be stored in a cool and dry area.
材料特点:抗溶解,耐磨蚀,高耐热,耐油,韧性良好
材料形式:颗粒料
加工方法:挤出,注射成型
塑料牌号:TPU S90A55N
定属记号:TPU-聚脂
销售电话:185 5121 3137 谭经理
湘樟版权:http://www.xzslw.com/sujiao/tpu/elastollan/s90a55n.html
胶料物性
物理性能 | 额定值 | 单位制 | 测试方法 |
比重 | 1.23 | g/cm³ | ASTM D792 |
硬度 | 额定值 | 单位制 | 测试方法 |
硬度计硬度(邵氏 A) | 92 | ASTM D2240 | |
机械性能 | 额定值 | 单位制 | 测试方法 |
拉伸模量 | 49.0 | MPa | ASTM D638 |
弯曲模量 | 53.8 | MPa | ASTM D790 |
抗泰伯磨耗(1000 g,H-18 转轮) | 25.0 | mg | ASTM D1044 |
弹性体 | 额定值 | 单位制 | 测试方法 |
拉伸应力 | ASTM D412 | ||
100%应变 | 10.3 | MPa | |
300%应变 | 20.0 | MPa | |
抗张强度(断裂) | 38.6 | MPa | ASTM D412 |
伸长率(断裂) | 540 | % | ASTM D412 |
撕裂强度2 | 128 | kN/m | ASTM D624 |
压缩永久变形 | ASTM D395B | ||
23℃,22.0 hr | 25 | % | |
70℃,22.0 hr | 45 | % | |
热性能 | 额定值 | 单位制 | 测试方法 |
玻璃转化温度(DSC) | -9.44 | ℃ | DSC |
维卡软化温度 | 132 | ℃ | ASTM D1525 |
补充信息 The value listed as Tensile Modulus ASTM D638,was tested in accordance with E-Modulus ASTM D412. |
|||
注射 | 额定值 | 单位制 | |
干燥温度 | 79.4 到 90.6 | ℃ | |
干燥时间 | 2.0 到 4.0 | hr | |
建议的最大水分含量 | 0.030 | % | |
加工(熔体)温度 | 193 到 216 | ℃ | |
挤出 | 额定值 | 单位制 | |
干燥温度 | 79.4 到 90.6 | ℃ | |
干燥时间 | 2.0 到 4.0 | hr | |
建议的最大水分含量 | 0.030 | % | |
熔体温度 | 188 到 210 | ℃ |